高吸油聚氨酯泡沫的制备与表征修改完成版.docVIP

毕业论文 所在学院： 专 业： 论文题目： 高吸油聚氨酯泡沫的制备与表征 摘要 本文以聚醚多元醇（N220、N330)和甲苯二异氰酸酯（TDI)为原料，采用一步发泡法，合成一种泡沫质地柔软、泡孔结构较好、且具有较高吸油性能的软质聚氨酯泡沫。研究了催化体系、TDI指数、物理发泡剂、聚醚多元醇、水、泡沫稳定剂等对泡孔结构和吸油性能的影响。得到了最佳工艺配方，即：聚醚多元醇100份，TDI指数103%，A33为4.8份，辛酸亚锡（T9）0.8份，泡沫稳定剂为4份，物理发泡剂（141b）20份，水10份。制得的泡沫结构较好时，对原油的吸油倍率为35g/g。 关键词 软质聚氨酯泡沫 高吸油 泡孔结构 Preparation and characterization of High oil absorption polyurethane foam ABSTRACT Polyether polyol (N220, N330) and toluene diisocyanate (TDI) as the raw material,using the one shot method, synthesis of a soft foam, a foam structure better, and has a high oil absorption properties of the flexible polyurethane foam.Studied the catalytic system, TDI index, the physical blowing agent, polyether polyol, water, foam stabilizers and cell structure of the oil performance.To obtain the optimum process recipe, namely: 100 parts polyether polyol, TDI index of 103%, A33 4.8 parts stannous octoate (T9) 0.8 parts to 4 parts of a foam stabilizer, the physical blowing agent (141b) 20 parts, 10 parts water.The foam structure is preferably obtained when the ratio of the crude oil was 35g / g. Key words : The flexible polyurethane foam, High oil absorption, Foam structure 摘要...............................................................................................................................I ABSTRACT..............................................................................................................II 第一章 绪论 1 1.1 引言 1 1.1.1 油类污染及危害 1 1.1.2 处理与预防油类的污染 2 1.2 传统吸油材料 2 1.2.1无机类吸油材料 3 1.2.2 有机类吸油材料 3 1.3 高吸油树脂概述 4 1.3.1 高吸油树脂简介 4 1.3.2 吸油材料的特性 4 1.3.3 吸油性树脂材料的合成 5 1.3.4 高吸油树脂的吸油机理 6 1.3.5 影响高吸油树脂材料吸油能力的影响因素 7 1.4 高吸油材料的应用 9 1.4.1 用于保护环境 9 1.4.2 作为芳香剂、诱虫剂等缓释剂基材 9 1.4.3 用于改性添加剂 9 1.4.4 用作密封材料 9 1.5 国内外聚氨酯树脂的发展概述 10 1.5.1 我国聚氨酯工业的发展 10 1.5.2 国外聚氨酯工业的发展 11 1.6 本论文研究的目的和意义 12 1.6.1 实验研究的意义 12 1.6.2 实验的目的 12 第二章 高吸油聚氨酯泡沫的制备与表征 13 2.1 前言 13 2.2 高吸油聚氨酯泡沫的制备原料 14 2.2.1 聚醚多元醇 14 2.2.2 异氰酸酯 15 2.2.3 催化剂 15 2.2.4 水 1