晶须概念的泛化与学术影响.pdfVIP

《化学通报》在线预览版 晶须概念的泛化与学术影响 1,2∗ 1 乌志明 马培华 1 2 （中国科学院青海盐湖研究所 西宁 810008 ； 中国科学院研究生院 北京 100039） 摘 要 最初只称单晶短纤维为晶须，稍后结晶较好的多晶纤维也被称为“晶须”，现在无定形纤维也归进 了晶须专著，通过对晶须概念泛化过程的反思，希图澄清学术著作中10多年来相沿的一个模糊认知。 关键词 晶须 纤维 Misapplications of Whisker-definition and its Academic Influences Wu Zhiming1,2 ， Ma Peihua1 1 ( . Qinghai Institute of Salt Lakes,Chinese Academy of Sciences, Xining 810008 2 . The Graduate School of the Chinese Academy of Sciences, Beijing 100039) Abstract Initially, crystal whiskers are only referred to single crystal short fibers, then comparatively well crystallized multi-fibers are also called “whiskers”, and till now, even the amorphic fibers are included in the category of whiskers. Considering the process of misapplication of whisker definition, this article is to clarify the obscure cognition which has become a custom through ten years of usage in the academic works and researches. Key words Whisker ，Fiber 纤维具有高度各向异性，在复合材料中得到广泛应用；晶须是高性能短纤维的一个典型代表，晶须因 高强度和显微增强特性，近 20 年已成为国内外学者研究甚多的一种增强纤维。10 多年来发表的许多“晶 须”方面的论著[1~3]一直在套用一个错误模式：开篇都会引述学术晶须的经典定义，而在引证别人的综述 或阐述自己的研究时，所述的往往又是并不符合学术晶须定义的“商业晶须”。一定意义上，传媒在支配 着我们的思想和感知。在学术上，我们不自觉地囿于庞大的互联网传媒之中，搞研究、写文章都麻木地在 套用一些固定的模式和思路，这个过程本身就埋没了太多本该有的个体灵性与创新。更致命的是，有可能 10 年或 20 年后才发现大家所通用的模式是不合理或错误的。 1 晶须概念限定与晶须研究的大众化 1.1 晶须概念限定与晶须研究大众化的矛盾 Evans 对晶须有个经典表述[4] ：晶须(Whiskers)是一种纤维状单晶体，横断面近乎一致，内外结构高度 完整，长径比一般在 5～1000 以上，直径通常在200nm～100μm 之间，但具有特殊性质的晶须直径一般在 1～10μm 之间。这是至今的著述[1~3]公认且一直引用的晶须定义，但引用后的相关内容都往往太广泛，甚 至大相庭径。 从该晶须定义可见，晶须首先是单晶。培养单晶已经不容易，再让特定的物质长成晶须，也就是长成 特定尺寸范围的纤维状单晶，更是难上加难。现实却似乎并非如此，随便浏