铌微合金化技术在大梁钢生产中的应用.pdfVIP

铌微合金化技术在大梁钢生产中的应用 廖 明 周远华 李 斌 俞海东 骆世雄 (重庆钢铁股份有限公司钢研所) 摘 要 本文介绍了重庆钢铁股份有限公司采用铌微合金化技术生产大梁钢(16MnL) 的实 践。找出了造成大梁钢品种改判的主要原因。着重分析讨论了影响大梁钢宽冷弯性能合格率 的主要因素，并有针对性地采取了一系列有效的技术管理措施，使大梁钢宽冷弯性能合格率 得到显著提高。 关键词 大梁钢 铌微合金化 宽冷弯合格率 THE APPLICATION OF Nb MICRO-ALLOYING TECHNOLOGY IN GIRDER STEEL PRODUCTION LIAO Ming ZHOU Yuanhua LI Bin YU Haidong LUO Shixiong (ChongQing Iron and Steel Co.Ltd Iron and Steel Institute) SYNOPSIS This paper introduces the practice of produce the girder steel adopting Nb MICRO-ALLOYING TECHNOLOGY about Chongqing Iron Steel Co.ltd. The mian reasons for causing girder-steel variety commuted have been found. The mian factors are emphasis analysed that influenced on width cold-bending qualified rate of girder steel. A series of measures have been taken about appropriate technology and adminstration in the light of above reasons, and width cold-bending qualified rate of girder steel have been increased by a big margin. KEYWORDS Girder steel Nb mircoalloy Width cold-bending qualified rate 1 前 言 大梁钢(16MnL)钢板主要用于制造汽车大梁、桥壳等重要器件，对其性能要 求较高，即不仅对强度有严格的要求，而且还对宽冷弯(d=a，b=35mm)和金相组 织(带状组织小于 3 级)有极为严格的要求。试生产初期，16MnL 钢热轧宽冷弯合 格率约为 50%~60%，改判率较高。通过公司相关单位共同协作、合力攻关，统 计分析了上千个生产工艺数据，检测和分析了几十个试样的低倍、金相、化学成 分，跟踪试验了几十批的 16MnL 钢生产情况，进行了多轮铌微合金化试验，找 出了影响宽冷弯不合的主要原因。制定并实施了相应的合理的成分和生产工艺方 案后，取得了良好的效果。目前 16MnL 钢热轧宽冷弯合格率在 90% 以上，且缩 短了交货周期，生产工艺顺行，大大减少了热处理工作量和改判 Q345A 钢的数 1 量，为企业赢得了良好信誉。 2 大梁钢的技术要求、生产工艺流程及生产现状 2.1 钢的牌号和熔炼化学成分 表 1 钢的牌号和熔炼化学成分 规格 化 学 成 分 % 牌号 mm C Si Mn P S Alt Nb C+1/4Mn 0.12 0.20 1.20 ≤ ≤ 0.020 0.008 ≥ 16MnL 6~14 ~0.17 ~0.55 ~1.60 0.02