离心风机堆焊焊条组织和耐磨性的研究.pdfVIP

ELECTRIC POWER 离心风机堆焊焊条组织和耐磨性的研究 An Investigation on Structure and Wear-resistance of Hardfacing EIectrodes for CentrifugaI Fan 徐向阳 (华北电力大学 机械系，河北 保定 07 1003) 摘 要：对电站锅炉离心风机常用的 种耐磨堆焊焊条进行试验研究。结果表明，在冲蚀磨损条件下，种焊 3 3 条的耐磨性有明显不同， 焊条的耐磨性优于 和高铬铸铁焊条；堆焊层的耐磨性随冲蚀角度而 Cr-W-V Cr-Mo-Si 变化是风机叶片不均匀磨损的主要原因；堆焊层硬度与耐磨性无简单对应关系，不宜作为堆焊条设计和选择的 主要依据。 关键词：离心风机；叶片；冲蚀磨损；堆焊焊条；耐磨性 Abstracts Three kinds of wear-resistant hardfacing electrodes often used for centrifugal fans of utility boilers are investigated. The results show that these electrodes are dramatically different in wear-resistance under the condition of erosion. Cr-W-V electrode shows higher erosion-resistance than Cr-Mo-Si and high chromium cast iron electrodes.The erosion-resistance varies with the erosive angle and this is a main reason for uneven wear of fan blades. The erosion-resistance of hardfacing overlay has not a simple relation with its hardness, consequently the hardfacing overlay cannot be regarded as a main basis for the design and selection elec- trodes. Key words centrifugal fan;blade;erosion;hardfacing electrode;wear-resistance 中图分类号： 文献标识码： 文章编号： （ ） TK223.26 B 1004-9649 2001 05-0004-03 风机是保证电站锅炉正常运行的关键设备之 一。因为引风机输送的是含有一定质量浓度SiO2 、 1 试验 Al O 和Fe O 等高硬度矿物质的烟气，排粉机输送 2 3 2 3 3 种焊条规格均为D4.0 mm ，焊前350 ℃烘干 1 的高浓度煤粉中也含有此类物质，所以风机叶轮 h 。使用直流焊机施焊，焊接电流I=160～180 A ，层间 （包括叶片和前后盘）的磨损都较严重。风机磨损 温度（ ） 。