京唐烧结铁矿粉同化性测试研究.pdfVIP

2014年炼铁精细化管理，挖潜补漏及新技术应用研讨会 会议论文集 京唐烧结铁矿粉同化性测试研究 1 1 2 1 1 王全乐 康海军 裴元东 石江山 袁中平 （1. 首钢京唐公司炼铁部，河北唐山 063200；2. 首钢技术研究院，北京 100043） 摘 要：烧结过程中铁矿粉的同化性是研究高温特性的重要部分，具有适宜同化性的铁矿粉，在烧结过程中液相粘 结良好，有利于烧结矿质量指标的改善。本文对京唐烧结用料中代表性的五种主料矿粉：巴卡粉、杨迪粉、巴烧粉、 澳粉和地方粉的同化性能进行了测试；并按两两搭搭配组合方式进行了同化性测试，发现不同矿粉两两搭配后，混 合粉的同化性均介于单种矿粉的同化性之间，并且混合矿同化性基本与单种矿比例呈现线性相关关系。 关键词：烧结；同化性；铁矿粉；配合 Research on assimilation of iron ore during sintering process for Jingtang WANG Quanle et al Abstract: Assimilation of iron ore powder sintering process is an important part of research on high temperature properties, with proper assimilation of iron ore powder, in the sintering process iquid phase bonding is good, being conducive to the improvement of sinter quality index. In this paper, five kinds of main representative raw materials in Jingtang were chosen: CAJ fines from Brazil, Yandi fines, Stardard fines from Brazil, PB fines and domestic concerntrate fines, and their assimilation performance were tested; and a combination of assimilation test according to two two was carried out. It can be found that assimilation of blended ore was between that of single ore, and there are good linearly relation between assimilation of blended ore and ratio of single ore. Key words: sinter；assimilation；iron ore；cooperation 前 言 烧结矿靠液相固结成矿，烧结过程中，随着温度的升高，粘附层内的铁矿粉与熔剂同化而形成熔相，然 后熔相逐渐增多，并继续同化粗粒核矿石，当熔相冷凝时最终形成非均相结构烧结矿。吴胜利等提出了同化性 的概念 [1-2]，通过定量测试铁矿粉与熔剂反应形成液相的能力来指导优化配矿，已取得广泛应用 [3-6]。 本文采用微型烧结试验装置，针对京唐烧结用几种典型主流矿种，巴卡粉、巴烧粉、澳粉、杨迪粉和地方粉， 在测试单种矿粉同化性基础上，进行了两两搭配测试，以期为指导京唐烧结配矿提供支持。 1 试验原料及方法 1.1 实验原料 京唐用5种主料总比例占烧结用料的70%以上，其化学全成分分析见表1。 表 1 京唐烧结主料化学全成分分析 T