奥氏体不锈钢SUS304带氧化皮直接轧制技术的研究.pdfVIP

奥氏体不锈钢 SUS304 带氧化皮直接 轧制技术的研究 何 慎 沈继程 江来珠 （宝钢研究院,上海 201900 ） 摘 要 通过在实验室对奥氏体不锈钢 SUS304 黑皮卷直接进行压下率分别为10%、20%、30%的冷轧然后退火酸 洗的试验，证明通过在热轧后进行一定压下率的直接轧制可以获得与No.1 产品相比晶粒尺寸等级相同、表面粗糙 度更低、力学性能和耐蚀性相近的 2E 产品。 关键词 奥氏体不锈钢 氧化皮 冷轧 Study on Direct Rolling of Hot Rolled Austenite Stainless Steel SUS304 with Oxide Scale He Shen Shen Jicheng Jiang Laizhu (RD Center, Baoshan Iron and Steel Co.,Ltd. ，Shanghai,201900) Abstract Cold rolling of hot rolled austenitic stainless steel SUS304 with oxide scale was carried out in laboratory. Different reductions were applied during cold rolling process, namely 10%, 20% and 30%. It has been proved that the surface of the cold rolled products after being annealed and pickled possesses lower surface roughness compared to the conventional hot rolled No.1 products, whereas the grain size, mechanical and anti-corrosion properties are comparable with those of No.1 products. Key words austenite stainless steel,oxide scale,cold rolling 1 引言 宝钢不锈钢分公司的不锈钢热带退火机组设置了六辊在线轧机 。其主要功能是在退火酸洗之前将带氧化 皮的黑皮卷轧至No.1 产品的最终厚度，不仅扩大产品的厚度范围，并且生产具有比No.1 更好表面的产品， 该生产工艺称为直接轧制，直接轧制后经退火酸洗的产品称为 2E 表面产品。该轧机的设计最大压下率为 30%[1] 。 本文重点研究直接轧制的压下率对2E 表面产品性能的影响以及2E 表面产品和No.1 表面产品性能 的对比。 2 试验方法 试验采用宝钢不锈钢分公司生产的SUS304 奥氏体不锈钢黑皮板，厚度为3mm 。其化学成分为见表1。 带氧化皮的试样进行单道次冷轧，压下率分别为 10%、20%和30% 。根据经验，冷轧后的试样在1050℃进 行固溶退火[2] 。 何慎，男，工学博士，电子邮箱：heshen@ 2007 中国钢铁年会论文集 表 1 试样化学成分质量分数 （wt% ） Tab. 1 Chemical compositions of as-received material （wt% ） 元素 C Si Mn N O