尾巨桉木材物理力学性质与主成分分析.docVIP

尾巨桉木材物理力学性质的主成分分析 苌姗姗 刘元 胡进波 （中南林学院工业学院　湖南长沙　410004） 摘 要：以11个尾巨桉家系、无性系木材物理力学性质测试数据为研究材料，通过SPSS数理统计软件运用主成分分析方法，将影响尾巨桉木材物理力学性质的9个指标分为强度指标和干缩指标两大主成分，而其中影响最大的是基本密度和差异干缩。为以后的尾巨桉工业用材的定向培育，提供了以基本密度和差异干缩为材质好坏的主要监测指标。 关键词：尾巨桉　木材物理力学性质　主成分分析 The Principal Component Analysis on the Physical and Strength Properties of E.urophylla譋.grandis Chang Shanr-shan, Liu Yuan, Hu Jin-bo (College of Industry of Central South Forestry University Changsha Hunan 410004) Abstract: The paper is based on the test data from the physical and strength properties of 11 E.urophylla譋.grandis families and Eh.urophylla譋.grandis clones. With principal component analysis, 9 factors of affecting the wood physical and strength properties are divided into two classes梥trength index, shrinkage index, of which the basic density and variance shrinkage are more important. It is good for the directive practice of the seed selection and directive breeding for E.urophylla譋.grandis. Key words: Ep.urophylla譋.grandis, physical and strength properties, principal component analysis g 尾巨桉(E.urophylla×E.grandis)是广西东门林场于1986年采用尾叶桉和巨桉杂交获得的第一批杂交种，其木材密度高、花纹美丽，是装饰和家具制造的良材，可广泛应用于家具、地板、耐久的结构材和建筑材的生产[1-2]。目前，在尾巨桉木材工业用材定向培育中，急需解决的问题是如何监控木材材质，及时调整营林措施，从而达到改善木材品质的目的。木材物理力学性质是木材科学加工与合理利用最重要的基础之一，常用测试的多项参数指标来表征，则衡量木材物理力学性质木材材质鉴定是一项很复杂的工作。然而，在实际生产中，如果按常规全部检测这些指标，工作量、花费很高，因而有必要从中筛选一些衡量木材材质的主要指标，作为材性选种和定向培育的主要目标，或作为材质监控的主要依据[3-5]。 1 材料与方法 1.1 试材情况 试材于2002年3月采自广西东门林场雷卡分场9林班54经营班，选取代号为DH2、DH12、DH16、DH18、DH19、DH30、DH32、DH33八个家系和代号为DH30-1、DH30-5、DH30-7三个无性系共30株样木，样木情况见表1。 表1 样木情况记录 27 5.7 DH30 1 15.1 23.6 11.7 2 18.7 26.3 7.6 2 16.2 24.2 14.4 3 16.8 23.9 5.4 3 14.6 18.8 9.6 DH12 1 17.7 25.1 12.2 DH32 1 16.1 28.7 17.4 2 15.3 22.4 22.4 2 16.2 26.2 15.2 3 18 26.2 12.9 3 16 23.3 13.5 DH16 1 16.1 23.3 4.8 DH33 1 16.6 28 11.2 2 19.4 26.1 5.8 2 17.2 28.6 12.8 3 17.2 24 6.2 3 15.9 15.9 9.6 DH18 1 16.8 26.4 4.4 DH30-1 1 15.9 26 13.2 2 16.5 23.8 6.2 2 18 27.6 18.2 3 17.5 25.9 11.5 DH30-5 1 15.3 22.6 9.7 DH19