电解法回收废镍基高温合金的研究.pdfVIP

电解法回收废镍基高温合金的研究 魏国侠1刘汉桥1孙 挺 2 1天津城市建设学院，天北大学理学院，辽宁沈阳110004 摘要：以镍基耐高温合金切削废料为可溶性阳极，采用隔膜电解法在氯化物体系中进行了电镍产品回收的研究， 考察了镍离子浓度、电流密度、电解液温度、极距等参数对槽电压、阴极能耗及阴极电流效率的影响，并通过 正交实验确定以阴极电流效率为目标的最佳电解条件：镍离子浓度为60g·L-1，电流密度为250A·m-2，电 解液温度为65℃，极距为25cm，在此条件下阴极电流效率超过95％以上。 关键词：镍；镍基合金；电解；回收 Studyonrecyclingnickelwithnickelsuperalloyscrapbyelectrolysis WEIGuoxia1 LIUHanqiao1 SUNTing2 1TianjinInstituteofUrbanConstruction,Tianjin300384,China;2Schoolof Science,NortheasternUniversity,Shenyang110004,Liaoning,China Abstract:Aprocessofrecoveringnickelwasprovidedwithnickelbasesuperalloyscrapassolventanodeusingmem braneelectrolysismethodsinchlorideelectrolytes.Theeffectofparameterssuchasnickelionconcentration,current density,temperatureandfieldpitchoncellvoltage,catholicenergyconsumedandcatholiccurrentefficiencywere respectivelystudied.Accordingtoorthogonaltestresultsofthegoalsofcatholiccurrentefficiency,optimization conditionsuchnickelionconcentrationas50g ·L-1,currentdensityas250A ·m-2,temperatureas65℃,field pitchas25cm,isconfirmed.Underthecondition,catholiccurrentefficiencyreachsabove95％ . Keywords:nicke;nickelsuperalloy;electrolysis;recycling 入硼酸后， f恒温水浴稠 看出随着电 加。当温唐 ．率从90.95 高到65℃I 1102I冶金工程 电阻增大，槽电压增加，阴极能耗增加。极距小 阴极电流效率分别达到95．96％、97．13％。 虽然能够降低槽电压，但容易发生短路现象(即 表3 阴极电流效率正交实验直观分析表 电流不通过电解液，直接由阳极流至阴极)，降 低电流效率(如图9所示)。而极距增加，槽电 试验钏2+浓擘电流密甓删C℃删D。。需…一 ’4 2…1 压相应增大，副反应增多，也会导致电流效率下 ／g·L1／A·m 降。实际电解生产极距应大于15cm。 。。。2 2 2