《化学通报》在线预览版 环境响应性凝胶的体积相变行为 李鑫* （嘉应学院化学系 广东梅州 514015 ） 摘 要 综述了温敏性聚合物的低临界溶解温度和温度响应性凝胶体积相变温度的相互关系、体积相变的影响因 素、体积相变的连续与否，并对如何调节凝胶的溶胀－收缩速率作了简要介绍。 关键词 低临界溶解温度 体积相变 连续与不连续 本体凝胶与微凝胶 Volume-Phase Transition Behavior of Environmentally Responsive Hydrogels Li Xin (Department of Chemistry , Jiaying University, Meizhou, Guangdong 514015) Abstract This paper reviewed the interrelations between lower critical solution temperature of temperature-responsive polymer and volume phase transition temperature of temperature-responsive hydrogels, the influence factors of volume phase transition and whether the volume phase transition is continuous or not. Besides, how to regulate the swelling-deswelling velocity of the responsive hydrogels was briefly introduced. Key words Lower critical solution temperature, Volume pha se transition, Continuous and discontinuous, Bulk gels and microgels 凝胶是一种介于固体和液体之间的物质形式，由交联成网状结构的聚合物吸收液体介质后 （称为溶胀溶剂）而成，其性质很大程度上取决于聚合物网络与溶胀溶剂的相互作用。环境响应 性凝胶则是指能对微小的环境变化如溶剂组成、温度、pH 、离子强度等做出响应的特殊凝胶，当 环境发生微小的变化时，凝胶将发生显著的可逆的溶胀或收缩，故又称之为智能凝胶。 1984 年， Tanaka [ 1 ] 首次报导了聚-N-异丙基丙烯酰胺（poly-N-isopropylacrylamide, 简称 PNIPAM ）凝胶在 人的生理温度附近（约 33.2 ℃）可发生显著的可逆体积相变，体积变化达几十倍甚至上百倍，因 而引起了广泛关注。实际上，N- 单取代或双取代的丙烯酰胺聚合物在一定程度上都具有温度敏感 性能。目前，对 N- 取代丙烯酰胺聚合物为基础的响应性凝胶的研究有两个方面：一是溶胀热力学， 主要是研究凝胶在溶胀/ 收缩过程中体积相变温度、溶胀率的影响因素及其调节；二是溶胀动力学， 即通过对凝胶的结构修饰来改变其溶胀/ 收缩的速率。 1 体积相变影响因素及其调节 1.1 聚合物组成对 LCST 和 Tvpt 的影响 李鑫 男，32 岁，博士，从事功能高分子合成与性能研究。E-mail ：mzlixin@ ，Tel ：0753-2186853 很多丙烯酰胺衍生物制备的线形聚合物在水中有一个低临界溶解温度(lower critical solution temperature, 简称 LCST) ，即低温时聚合物溶于水形成稳定的均相溶液，温度超过 LCST 后就不溶 而发生相分离，所以 LCST 是聚合物溶液发生相分离的临界温度；若在聚合过程中加入交联剂制 成网状聚合物，便得到具有特定的体积相变温度(Volume Pha