毫秒级钨系延期药的研制与应用 阎巧玲，许 勇 （西安庆华民用爆破器材公司，陕西西安 710025 ） 摘要：采用亚纳米钨粉作可燃剂及无毒氧化物作缓燃剂，研制出了延期时间稳定、精度较高的新型毫秒级延期药， 使钨系延期药的燃速从传统的秒级(2～6.5s/cm)到了毫秒级(200～1 300 ms/cm)。另外，由于纳米钨粉的活性大， 使药剂的发火点降低，克服了钨系药点火困难的问题，实现了点火－延期一体化。通过在毫秒级导爆管延期雷管 中的应用，该药剂相对于燃速1 000 ms/cm 左右的硅系药、硼系药不需要加点火元件，能够被导爆管直接点燃， 简化了产品装配过程，具有良好的经济效益和应用前景。 关键词：亚纳米级钨粉；氧化铁；点火－延期一体化；钨粉粒度 Research and Application of Millisecond Tungsten Type Delay Charge YAN Qiaoling, XU Yong (Xi’an Qinghua Research Institute of Industrial Exprosive Material, Xi’an, 710025, China) Abstract: The new Tungsten type delay composition with the reliable function time and the higher delay precision was researched by nanometer Tungsten power and nonhazardous Ferric Oxide. The burning rate of tungsten type delay composition from the second traditional (1500～6500ms/cm) to the millisecond level (200 ～1300ms/cm).The results show the new Tungsten type millisecond delay composition can solve effectively ignition- delay integral whole turns, and have the good economic performance and the certain application limits In Millisecond Cup-type Detonator by the tests.. Keywords: nanometer tungsten power, ferric oxide, ignition-delay integral, tungsten power granularity 目前，国内毫秒级延期雷管大多采用的是硅系、硼系延期药，这两类药剂在低段产品中作用可靠，延 时精度高，应用于高段产品时，需要加点火元件才能有效作用[1] 。加了点火元件后，整个延期系统就会出 现两个预点火过程，不仅影响雷管延时精度，而且使装配工艺变得复杂，生产成本增大。为了有效解决点 火、延时两者之间的矛盾，研制既能满足延时需要，又能被导爆管直接点燃的新型毫秒延期药，是企业一 直努力欲实现的目标。 钨系延期药是一种能够批量化生产的微气体药剂，具有燃速可调范围大、贮存性能良好等优点，作为 慢燃速药剂在军、民品领域中应用广泛[2] 。随着超细钨粉加工工艺的成熟，极大地扩展了钨系延期药的开 发应用空间。经过几年的探索和实践，以先进的粉体加工技术为依托，研制出了新型纳米钨系毫秒延期药， 取得了较好的应用效果。 作者简介：阎巧玲，女，工程师，从事延期技术的研究；电话 1 理论依据 延期药作为传爆序列中的成