超快速冷却HRB500Ⅳ螺纹钢筋的生产.pdfVIP

超快速冷却 HRB500Ⅳ螺纹钢筋的生产 蒋艳菊 （本溪北营钢铁（集团）公司钢研所，本溪 117017 ） 摘 要 本文利用 20MnSiNb 钢，通过轧后穿水冷却工艺，使φ 16 ㎜钢筋力学性能达到了 HRB500 钢筋要求。为今 后 500MPa 级螺纹钢筋生产,奠定了基础。试验认为钢筋强度增加，主要源于细晶强化和相变强化。 关键词 HRB500 螺纹钢筋 穿水冷却 The Manufacturing Technology of the Extra-fast Cooling Hot-rolled Ribbed Bars Grade Ⅳ(500MPa) Jiang Yanju (Steel Reseach Institute,Benxi Beiying Iron Steel (Group) Co.,Ltd. ，Benxi,117017) Abstract The essay briefly introduces the water-cooling technology applied in the manufacturing process of the hot-rolled ribbed bars of 20MnSiNb.The mechanical property of the steel bars in the nominal diameter of 16mm meets the requirement of the Hot-rolled ribbed bars Grade Ⅳ(500MPa) which provides the theoretical basis for the production of the hot-rolled bars of 500MPa.The test result shows that the grain-refining and the transition contributes to the increase of the strength.1 Key words HRB500,ribbed bars,ultra-acclerating water cooling technology 1 引言 近年来，中国的螺纹钢筋产量和用量，一直维持在 7000 万 t 左右，并呈逐年增长趋势。预计今后 20～ 30 年，这种局面将会延续。可是，由于传统设计理念的作用，国内螺纹钢筋的使用，80%以上仍为屈服强 度较低的Ⅱ级钢筋，这与工业发达国家广泛使用 400MPa 级以上的高强度钢筋形成鲜明对照。在建设部大力 推动下，国内Ⅲ螺纹钢筋应用逐年增加，但 500MPa 级的Ⅳ级螺纹钢筋的生产和应用仍处于起步阶段。本溪 北营钢铁公司，利用 20MnSi 钢进行轧后余热处理生产Ⅲ级钢筋的过程中，曾用 20MnSiNb 进行 500MPa 级 钢筋试制。结果表明，利用 20MnSiNb 钢轧后穿水冷却工艺，可使该钢的屈服强度增加近 50～100MPa，即 达到了Ⅳ级螺纹钢筋的强度水平。 2 钢筋的成分及力学性能 试生产的 HRB500 钢筋的化学成分，采用 GB1499—1998 标准中 20MnSiNb 钢的成分。该钢是 HRB400 钢筋的推荐成分。钢筋的力学性能按 HRB500 钢筋的性能要求生产（表 1）。 1蒋艳菊（1978—）女，1999 年毕业于鞍山钢铁学院，现在北营钢研所工作。 8-68 第八届（2011 ）中国钢铁年会论文集 表 1 HRB500 钢筋的化学成分及力学性能 牌号 C≤ Si≤ Mn ≤ P ≤ S≤ Ceq≤ R /MPa R /MPa A/% eL m