液相法纳米氧化铝粉体制备 作者：金祥 摘 要：工业上制取纳米Al2O3的一般方法可重复性差，且耗能大。本试验尝试以氯化铝、氨水与无水乙醇为主要原料使用液相法制取纳米三氧化二铝，研究不同溶液浓度、混合强度、焙烧温度下得到的纳米粉体粒径分布，以期改善工业制取纳米Al2O3的弊端。试验结果表明，在1.2 mol/L的AlCl3的乙醇水溶液下，配合1400 r/min的混合强度及1000 ℃的焙烧温度可获取20 nm左右的纳米Al2O3。 焙烧 粒径 Liquid phase method of nano alumina powder preparation Abstract：eneral methods of preparing nano Al2O3 on the industry have poor reproducibility and high energy consumption.In this experiment, with aluminum chloride,ammonia and ethanol as main raw materials, nano aluminum oxide was prepared by liquid phase method.Meanwhile,to improve drawbacks of the industrial preparation of nanometer Al2O3, we discussed effects of different solution concentration, mixing intensity, roasting temperature on nano powder particle size distribution. The test results showed that, in the ethanol water solution with 1.2 mol/L AlCl3, with mixing intensity 1400 r/min and calcination temperature of 1000 ℃ ,we could obtain nano Al2O3 about particle size of 20 nm. Key words：Nano hybrid roasting particle size0 前言 氧化铝，白色粉末状物体，且无定型，化学式为Al2O3，分子量为101.96。一般称为“铝氧”，不与水相容，矾土、刚玉是其俗称。纳米氧化铝是白色晶体状粉末，目前已经证实有 α、β、γ、δ、η、θ、κ和χ等十一种晶体。工业上不同的制备工艺和制备方法条件可以获得不同结构的纳米氧化铝。比如χ、β、η和γ型氧化铝，属于活性纳米氧化铝，具有多孔性，高分散、高活性等特点；κ、δ、θ、α型，不属于活性氧化铝，其比表面低，具有耐高温的惰性，几乎没有催化活性；β、γ型，的比表面较大，孔隙率高、耐热性强，成型性好，具有较强的表面酸性和一定的表面碱性，被广泛应用作催化剂和催化剂载体等新的绿色化学材料。该纳米氧化铝显白色蓬松粉末状态，晶型是γ-Al2O3。粒径是20 nm；比表面积≥230 m2/g。粒度分布均匀、纯度高、极好分散，其比表面高，具有耐高温的惰性，高活性，属活性氧化铝；多孔性；硬度高、尺寸稳定性好，可广泛应用于各种塑料、橡胶、陶瓷、耐火材料等产品的补强增韧，特别是提高陶瓷的致密性、光洁度、冷热疲劳性、断裂韧性、抗蠕变性能和高分子材料产品的耐磨性能尤为显著。极好分散，在溶剂水里面；溶剂乙醇、丙醇、丙二醇、异丙醇、乙二醇单丁醚、丙酮、丁酮、苯、二甲苯内，不需加分散剂，搅拌搅拌即可以充分的分散均匀。在环氧树脂，塑料等中，极好添加使用。 下面我们设反应物为a、b，生成物为c、d、沉淀固体为e。以下的固体沉淀粒子析出机理可以说明沉淀过程。设C1、C2、C3分别为ABC的浓度（D浓度影响较小，略去）。 a+b=c+d+e↓ 图1 AB两液空间分布图 图1为t=0时，即初始时刻时A液与B液中a与b的浓度C10、C20空间分布图。当混合过程开始时，a与b开始分别向对方的区域进行扩散，且在相遇后发生反应。 图2 图2为t=t时，即反应过程达到t时刻a、b和e沉淀物的浓度分布C1、C2、C的曲线，且当C超过一个浓度（临界成核浓度）CK时，在ab这个空间区域内有固体粒子析出。 图3 Lamer图 从液相反应固体析出粒子机理可以看出，如果想得到小粒径的胶粒就必须加大成核数，而要加大成核数就必须要使AB两液在足够短的时间内有足够或者说尽可能大的交界面，