助表面活性剂对微乳液法制备氧化锌的影响.DOCVIP

助表面活性剂对微乳液法制备氧化锌的影响 作者 金祥 摘 要：纳米氧化锌作为一种重要的无机材料，有许多特殊的性质，如非迁移性、荧光性、压电性、吸收和散射紫外线能力等，利用其在光、电、磁、敏感等方面的奇妙性能，可制造气体传感器、荧光体、变阻器、紫外线遮蔽材料、图像记录材料、压电材料、压敏电阻、高效催化剂、磁性材料和塑料薄膜等The Effect of Cosufactant on the Preparation of ZnO By Microemulsion Abstract ：Nano ZnO as an important inorganic materials, There are many special properties, such as non-migratory, fluorescence, piezoelectric, UV absorption and scattering ability, using its wonderful performance in the optical, electrical, magnetic, and other sensitive areas, can produce gas sensors, phosphors, rheostat UV shielding materials, image recording materials, piezoelectric materials, varistors materials, efficient catalysts, magnetic materials and plastic film and so on, having a very wide range of applications. In this experiment ,Zn (NO3) 2? 6H2O, NH3? H2O as raw materials, OP-10 and TX-100 as surfactant to prepare nano-zinc oxide powder by microemulsion. Then use XRD and DTA-TGA to characteristic and analysis the particle size. Key words：Zinc Oxide microemulsion poder 0 前言 微乳液即两种或两种以上互不相溶液体经混合乳化后，分散液滴的直径在5 nm~100 nm之间的混合液体[1]。微乳液为透明分散体系，其形成与胶束的加溶作用有关，又称为“被溶胀的胶束溶液”或“胶束乳液”。简称乳液。通常由油、水、表面活性剂、助表面活性剂和电解质等组成的透明或半透明的液状稳定体系。其特点是分散相的质点大小在10～100 nm间，质点大小均匀，显微镜不可见；质点呈球状；微乳液呈半透明至透明，热力学稳定，如果体系透明，流动性良好，且用离心机100 g的离心加速度分离五分钟不分层即可认为是微乳液[2]；与油、水在一定范围内可混溶。分散相为油、分散介质为水的体系称为O/W型微乳状液，反之则称为W/O型微乳状液。微乳液一般需加较大量的表面活性剂，并需加入辅助表面活性剂（如极性有机物，一般为醇类）方能形成。 纳米级氧化锌的突出特点在于产品粒子为纳米级，同时具有纳米材料和传统氧化锌的双重特性。与传统氧化锌产品相比，其比表面积大、化学活性高，产品细度、化学纯度和粒子形状可以根据需要进行调整，并且具有光化学效应和较好的遮蔽紫外线性能，其紫外线遮蔽率高达98 %，因此其广泛应用于化妆品中，用于化妆品的制备。另外在橡胶、陶瓷、纺织、国防涂料等领域也有广泛的应用[3]。 纳米ZnO的制备方法很多，包括化学气相沉积法、均相沉积法、溶胶-凝胶法、水热合成法等[4]。采用微乳液法制备纳米氧化锌，易于实现生产的工业化，相比于其它方法具有生产装置简单、操作容易、产物粒子分布均匀、粒径可控和不易团聚等优点，可用于规模化生产粒度均一的纳米粒子，因此拥有良好的研究前景[5]。 图1 纳米氧化锌制备的实验流程图 1.2 实验原理 微乳体系中单分散体系的油或水的液滴在连续相中不断扩散并相互碰撞，这种动力学结构使其成为良好的纳米反应器[6]，虽然这些小液滴会相互结合形成一些比较大的液滴，但是由于表面活性剂的存在，他们会重新分离形成较小的液滴，这种性质致使体系中液滴的直径和数目不随时间的改变而改变，成为一个非常稳定的反应体系，因此可以利用微乳液体系的这种特性合成纳米氧化锌[7]。微乳液仅仅是一个微反应器，其中的物质并不参与直接的反应，因此在反应过程中只发生了如下反应：