Y2O3含量对热压烧结AIN-玻璃碳复相材料性能的影响.pdfVIP

· 电 子 陶 瓷 、陶 瓷 一金 属 封 接 专 辑 · Y2o3含量对热压烧结AIN-玻璃碳复相 材料性能的影响 陆万泽，李晓云，丘 泰 ，袁文杰 (南京工业大学材料科学与工程学院，江苏 南京 210009) EffectsofY2O3ContentonPropertiesofAIN—GlassyCarbon CompositesbyHot—PressingSintering LU Wan—ze，LIXiao—yun，QIU Tai，YUAN Wen—jie (CollegeofMaterialsScienceandEngineering，NanjingTechUniversity，Nanjing210009，China) Abstract：A1N～glassycarboncompositeswerepreparedbyhot—pressingsinteringinN2atmosphere，U— singaluminum nitrideandglassycarbonasraw material，Y2O3asadditives．TheeffectsofYz03contenton sinteringproperties，phasecomposition，microstructure，mechanicalpropertiesandthermalconductivityof thecompositeswereinvestigated．Theresultsshow thatasthecontentofY203increasing，thebulkdensi— tyincreasesandapparentporosity decreasegradually．Y2O3occurredreaction and generating Y3A15012 withA12O3ofsurfaceofA1N，thenYaA15012occurredfurtherreactionandgeneratingYA103with Y2O3． W iththeincreaseofY203content，thebonding strength ofbetween glassycarbonandaluminum nitride grainincreased．Thebending strength graduallyreducedand the fracturetoughnessgradually decreased． W hen thecontentofY2O3is3 (wt)，thebendingstrengthofsampleisupto459．7MPa，whichwasthe highestandthefracturetoughnessmaximum is4．38．W henthecontentofY2O3is7 ，thehighestther— malconductivityofthecompositesis103．7W ·m ·K～ ． Keywords：Aluminum nitride，Glassycarbon，Hot—pressingsintering，Thermalconductivity 摘要：采用热压烧结工艺，以氮化铝和玻璃碳为原料、Y。0。作烧结助剂，在氮气氛下烧结制备AIN一玻璃碳复相材料。研 究了烧结助剂含量对复相材料 的烧结性能、相组成、显微结构、力学性能以及热导率 的影响。结果表 明：随着 Y0。含量 的增 加 ，试样 的体积密度逐渐增大，气孔率稍微减小。Y0。与 A1N表面 的Alz()。反应生成 Y。A10。，且生成 的Y。A1() 进一步 与 Yz0。反应生成 YAl0。。随着 Y。0。含量的增加 ，玻璃碳与氮化铝晶粒之间的结合强度增大，材料 的抗弯强度逐渐 降低 ，断 裂韧性逐渐减小 。当Y0。含量为 3 (质量 比)时，试样的抗弯强度最高为 459．7MPa，断裂韧性最大为 4．38；当Yz0 的含 量为 7 时 ，