烧结矿黏结相熔化特性地研究.pdfVIP

烧结矿黏结相熔化特性的研究 烧结矿黏结相熔化特性的研究 李光森 金明芳 姜 鑫 储满生 沈峰满 （东北大学材料与冶金学院，沈阳 110004） 摘 要 本文以高碱度烧结矿中的铁酸盐黏结相为研究对象，考察了黏结相的熔化特性随黏结相组成的变化规律。 通过试验探讨了不同n :n 以及MgO 、SiO 和Al O 含量铁酸盐黏结相的熔化特性。结果表明，n :n =1:1 CaO Fe2O3 2 2 3 CaO Fe2O3 时，黏结相的熔化温度最低，熔化时间最短；添加 MgO 黏结相的熔化温度升高，熔化时间变长；当 SiO2 含量为 3%时，黏结相的熔化温度最低，熔化最快；当 Al O 含量为 3%时，黏结相的熔化温度最低，熔化最快。 2 3 关键词 烧结矿 黏结相 熔化温度 熔化时间 Melting Characteristics of Binding Phase in Sinter Li Guangsen Jin Mingfang Jiang Xin Chu Mansheng Shen Fengman (Northeastern University, Shenyang, 110004) Abstract This paper studied the melting characteristics of binding phase in high-basicity sinter and got the relationship between the melting temperature and binding phase’s composition. By changing nCaO:nFe O , MgO, SiO2 2 3 and Al O percentage, the melting characteristics of binding phase were discussed. The results indicated that melting 2 3 temperature was the lowest and melting time was the shortest at nCaO:nFe2O3=1:1, adding MgO increased the melting temperature and melting time, at 3% SiO or 3% Al O the melting temperature and melting time were the lowest. 2 2 3 Key words sinter, binding phase, melting temperature, melting time 固相反应是烧结矿烧结成块的基础，高碱度烧结矿作为高炉炼铁的主要炉料，是以铁酸钙为主要黏 结相[1] 。由于铁精矿自身特性各不相同，其在烧结过程中的高温行为和作用亦有差别，会形成不同成分 的铁酸盐黏结相[2] 。因此，研究解明铁酸盐黏结相的化学组成对其熔化特性的影响，对指导烧结配料和 提高烧结矿强度具有重要的指导意义[3] 。 1 试验方法 本试验采用座滴法，如图1 所示，根据试样的形态，采集黏结相在不同温度下的照片，进而考察黏结相 的熔化特性。