单组份热固化环氧树脂灌封胶.pdfVIP

SLONT 2781 Hardener One Component, Flexible, Heat Cure Epoxy System Product Description SLONT 2781 is a clear, one-component, flexible, heat cure epoxy system designed for coil impregnation, and potting applications requiring low viscosity and minimal thermal stress. Properties Uncured COLOR, VISUAL: Clear VISCOSITY, cps: 1,350 ASTM D2393 SPECIFIC GRAVITY: 1.04 o POT LIFE @ 70 C., hours: 24 o POT LIFE @ 100 C., hours: 1.5-2 POT LIFE @ 110oC., hours: 1-1.5 o POT LIFE @ 115 C., hours: 3/4 o SHELF LIFE @ 25 C, months: 3 Properties Cured PHYSICAL HARDNESS, DUROMETER Shore D : 40 ASTM D 2240 TENSILE STRENGTH, psi: 5,500 ASTM D 638 TENSILE ELONGATION, %: 40 ASTM D 638 o -6 COEFFICIENT OF THERMAL EXPANSION, C: 77 x 10 2 o THERMAL CONDUCTIVITY, BTU-in/ ft hr F : 1.8 USEFUL TEMPERATURE RANGE, oC: -55 to 155* Electrical DIELECTRIC STRENGTH, volts/mil: 410 ASTM D 149 DIELECTRIC CONSTANT, 1 KHz: 4 ASTM D 150 DISSIPATION FACTOR, 1 KHz: 0.01 ASTM D 150 14 VOLUME RESISTIVITY, ohm-cm: 3.4 x 10 ASTM D 257 *NOTE: See Cure Schedule for requirements to achieve high temperature resistance properties. Mixing Instructions o o 1. Preheat coil, transformer or unit for 1 - 2 hours @120 C - 135 C. Allow to cool to approximately o 50 C. 2. Any surfaces such as terminal leads or mounting brackets were bonding is impractical, should be coated with a suitable epoxy release agent. 3. Pour SLONT 2781 into a unit or tank. If dipping application, units should be drained prior to curing. Cure Schedule Dipped Units o 6 - 8 hours @ 95 C – lowest shrinkage o 3 - 5 hours @ 105 C o 2 - 3 hours @ 120 C o * Post cure 2 hours @ 150 C for optimum high temperature properties. Storage Requirements One component epoxies are pre-catalyzed and have a limited shelf-life. Storage at elevated temperatures will result in a shortened shelf-life and premature gelation. Store material in a cool place. Date 08/2006 IMPORTANT: HEALTH CAUTION: The following supersedes any provision in your company’s