600MW+超临界锅炉TP347H+屏式过热器管抗高温蒸汽氧化腐蚀探讨.pdfVIP

600MW超临界锅炉TP347H屏式过热器管 抗高温蒸汽氧化腐蚀探讨 邓勇 刘盛波 彭芳芳 杨首恩 （四川出入境检验检疫局，东方锅炉（集团）股份有限公司，成都，610041） 摘要：本文针对某电厂 600MW超临界锅炉中 TP347H屏式过热器管在运行 5000h后出现大 量内壁氧化皮的现象进行了综合分析，结果表明：氧化皮致密层中的 Cr含量高于疏松层及基 体，有助于延缓管材的氧化,造成严重氧化的原因可能与超温运行和加氧运行有关，后来电厂 在运行中采取一定的保护措施，继续运行到 10000 小时后，割管分析证实了分析结果是正确 的，氧化状况得到明显改善。 主题词：超临界 氧化皮 抗氧化性能 Abstract: This article analyses the phenomenon synthetically, which there were so much oxide in internal surface of the TP347H panel division super-heater tubes after operation 5000h in certain 600MW super-critical boiler. The result indicated Cr content in the compact layer of scale was higher than that in the loose layer and the base. This structure was of benefit to oxidation resistance. The reasons of causing serious oxidation may be related to operation at overrun-temperature and operation with oxygen. The power station took some protection measures in operation according to above mentioned. The analysis of the tube cut from the boiler proved the result of this article was correct and the oxidation resistance was improved obviously, when the boiler operated continuously till 10000h. Subject: super-critical scale oxidation resistance property 1 简述 由我国自行设计建造的超临界锅炉近年来开始投入运行，对超临界环境下的 TP347H 抗高 温蒸汽腐蚀的性能尚未深入研究，某电厂 600MW 超临界燃煤锅炉在运行 5000 小时后，从过热 器弯头割管发现 TP347H管子内表面氧化严重，氧化皮脱落明显，最多的一根脱落氧化皮重量 达 78 克，容易造成堵塞而引发事故，从该部件上截取样管，对样管内表面氧化层及脱落的氧 化皮进行了分析研究并通报电厂，随后电厂在以后的运行中采取了一些措施，比如：尽量减 少启停次数，启停时注意控制升降温速度，严格控制水中的含氧量，不允许采用加氧运行方 式，严防超温运行等。在运行 10000 小时后再次割管，氧化情况明显好转，最多的一根发现 7 克脱落氧化皮，验证了最初的分析研究结论和采取的措施是正确的。 分析的重点分四个部分，前三个部分主要是针对运行时间 5000 小时后的样品进行的，一 是金属基体的常规分析，二是 TP347H 内壁氧化膜的分析，三是在弯头处位收集到的从管子内 壁脱落的氧化皮的分析，第四部分为运行 10000 小时后的样品的情况，验证前面的分析结果。 - 28 - 2 样管的常规分析 2.1 化学成分分析 在管样上截取试样，采用直读光谱进行化学成分分析，分析结果表明屏式过热器用 TP347H