杨木多层实木复合地板表板增强研究 贾翀 吴羽飞徐德良崔举庆 张洋 摘 要：为提高杨木多层实木复合地板表板的物理力学性能，采用真空处理的方法将三聚氰胺树脂(MF)浸 渍杨木，再对MF浸渍杨木地板基材进行压缩处理，从而使速生杨木的物理力学性能有较大提高。试验结果 表明：当真空度为0.05MPa，浸胶时间从1h增加到5h时，杨木增重率明显上升，其强度和尺寸稳定性能显著提 高；并确定了最佳压缩温度为195℃，压缩时间为30min，压缩率为45％。 关键词：三聚氰胺树脂杨木地板压缩处理 AStudyonmanufacturingreinforcedsurfaceboardofMulti-PlyParquet JiaChong WuYufei XuDeliangCuiJuqingZhangYang CollegeofWoodandScience,NanjingForestryUniversity,Nanjing210037 Abstract:Inordertoimprovethephysicalandmechanicalpropertiesofmulti-plyparquet,The methodofvacuumtreatmentwasusedtoimpregnateMFresinintopoplarcompositeflooring, thenitwascompressed,soastoincreasepropertiesofpoplarcompositeflooringr.Theresults showsthatffvacuumdegreeis0.05MPaandtheimpregnatedtimeisfromlhto5h,the weightofpoplarrisesclearlyanditsstrengthanddimensionalstabilityarealsoincreased. Optimumcompressedtemperatureis195℃ andcompressedtimeis30minandcompressedrateis 45％. Keywords:MFResin, poplarcompositeflooring,CompressedTreatment,Technology,Property 贾翀 南京林业大学木材工业学院，江苏210037 第六届中国木材保护大会暨2012中国景观木竹结构与材料产业发展高峰论坛 论文集 聚氰胺树脂(MF)浸渍到杨木地板基材中，再通过压缩处理，从而使得杨木地板基材在表面外观基本不变的条件 下，增加其密度，提高其物理力学性能，使得压缩后的杨木地板基材可取代优质木材应用到地板领域中去，提高杨 木自身的产品附加值。 1材料与方法 1．1试验材料 人工林I一74杨，来源于江苏宿迁市郊区，树龄5年，平均直径约20cm，按照试验设计要求将杨木锯解成一定尺 寸的试件，再对试件进行干燥和刨光，控制其含水率为8-10％。试验所用的三聚氰胺树脂来源于浸渍纸饰面人造板 厂，其外观为无色透明液体，固含量52．％，粘度45mpa．s，PH值为9。 1．2试验方法 试验时将杨木地板基材试件放入真空干燥器中进行不同条件下的真空处理，然后注入三聚氰胺树脂，进行浸渍 处理，处理一定时间后，取出试件进行适当干燥，使其保留所需的残留挥发份，再送入热压机进行压缩处理，处理 后的试件参照国家有关标准进行检测。 2结果与分析 2．1浸溃时间与各指标之间关系 浸渍时间是使得三聚氰胺树脂浸渍进入杨木木材内部的保障，在0．05MPa的真空度条件下，当浸渍时间从lh增 加到5h肘，木材的增重率从29．5％增加至54．2％，并随着时间的增长呈现先迅速增重后缓慢增重的趋势，木材是多 孔材料，在真空的作用下，容器内部形成负压，则导致木材表面与内部之间的压力差增大，从而使得胶液从木材的 外部向内部流动，其过程与木材吸湿过程相接近，当内部的胶液增多时，和外部胶液的压力差变小，则吸收胶液的 能力下降，从宏观上体现为增重速率降低。 同时，木材的阻湿率也随着木材增重率的增加而增加，木材阻湿率可以反应木材的耐水能力，木材的纤维素和 半纤维素分子上存在着一定量的亲水基团羟基(—OH)，由于这些羟基的主要作用，杨木随着外界温度和湿度的变 化，蒸发或吸收水分，产