掺聚羧酸系高效减水剂新拌耐久性溷凝土中_冒泡_现象的分析.pdfVIP

第 卷 年第 期 T 技术园地 28 2010 7 echnical Scope 掺聚羧酸系高效减水剂 新拌耐久性混凝土中 “冒泡”现象的分析 郑耕心 （中铁二十四局福建公司，福建福州350013） 【摘要】 聚羧酸系高效减水剂是目前铁路客运专线工程耐久性混凝土施工中常用的高效减水剂，使用效果良好，但也存 在一些问题。针对聚羧酸系高效减水剂在配制耐久性混凝土时常出现的“冒泡”现象，进行了原因分析，并提出解决办法。 【关键词】 聚羧酸系高效减水剂；耐久性混凝土；冒泡 【中图分类号】 TU528.042.2 【文献标识码】 A 【文章编号】 1671－3702 （2010）07－0031－02 Analysis of Bubbling Phenomenon in New Stir Durability Concrete with Poly-Carboxylic High Effective Water-Reducer ZHENG Geng-xin (China Railway Group No.24 Office Fujian Company, Fuzhou 350013, China) Abstract: Poly-carboxylic high effective water-reducer is a common water-reducer in the durability concrete construction in the railway transport of passenger project, the effect of which is good, but also some problems exist. Aiming at the phenomenon that poly- “ “ carboxylic high effective water-reducer often bubbling when mixing the durability concrete, the reason of which is analyzed, the so－ lution method is put forward. Keywords: poly-carboxylic water-reducer; durability concrete; bubbling 福州火车站改扩建工程的主体结构多采用耐久性 泡”现象。为此，笔者分别从原材料和配合比两方面查 混凝土，混凝土强度等级为C40。混凝土原材料为： 找原因，并对有关问题进行了研究。 水泥：台泥牌P.O42.5 普通硅酸盐水泥，福州台泥 1 聚羧酸高效减水剂的作用机理 水泥有限公司生产； 1）减水作用机理 骨料：石子粒径为5～31.5mm ，中砂细度模数为 聚羧酸类聚合物对水泥的作用，主要是由羧基 2.7 ，均为福州宏华砂石厂生产； （—COOH）、羟基（—OH）、胺基（—NH）和聚氧烷基 粉煤灰：Ⅱ级粉煤灰，长乐华能电厂生产； （—O—R）等与水亲和力强的极性基团，通过吸附、分 n 矿渣微粉：S95 级矿渣微粉，福建益材生产； 散、润湿、润滑等表面活性作用，对水泥颗粒提供分散 外加剂：HPCA －600 高效减水剂（为聚羧酸系高