连铸浸入式水口用镁铝尖晶石耐材地研究.pdfVIP

连铸浸入式水口用镁铝尖晶石耐材的研究 杨俊瑞 陈晓芳 樊新丽 胡丽敏 (中钢集团耐火材料有限公司，洛阳471039) 摘要：本文以烧结镁铝尖晶石为骨料，以镁砂和d—A1203为基质料，通过固相反应烧结法合成了浸入式水El用镁铝尖晶石耐火材 料，研究了基质含量和成型压力对试样显气孑L率、体积密度、耐压强度及抗热震性能的影响，结果表明：在200MPa压力下成型，经 1650。C x4h烧成，可以合成显气孔率为16，14％，体积密度为2．899／cm3的尖晶石耐火材料。 关键词：连铸；浸入式水口：镁铝尖晶石 Researchon for Magnesia-AluminaSpinelRefractory theContinuous Nozzle CastingSubmerged Yang Chen FanxinliHulimin junrui xiaofang 47 (SniosteelrefractoryCo．，LTD．Luoyang1039) this andaluminawereusedas andma— Abstract：In aggregate paper，magnesia—aluminaspinel，‘magnesi’a trix the of reactionsinte- materials，respectively，forsynthesismagnesia—aluminaspinelrefractoryby effectofmatrixmaterialscontentand on ring．The shapingpressureapparentporosity，bulkdensity，tom— showthatwhile andthermalshockresistancewerestudied．Theresults pressivestrength shapingpressure was refractorieswith of of2．89 wereob— 16．14％，bulkdensity g／cm3 200MPa，spinel apparentporosity tainedafter at1650。(：for4hours． sintering Keywords：Continuouscasting；thesubmergednozzle；magnesia—aluminaspinel -．IJL．--JL 刖昌 浸入式水口的使用寿命是衡量连续铸钢生产效率的一个重要指标¨。1。在浇铸过程中，浸入式水lZl饱受高 温钢水的冲刷和保护渣的侵蚀，还常常因氧化铝的粘附而发生堵塞，降低了水口的使用寿命，并恶化了钢坯的质 量。因此，开发具有防止氧化铝附着和洁净钢水双重作用的浸入式水口用耐火材料，对于连铸的顺行以及洁净钢 的生产有着十分重要的意义。 作为连铸复合式水口的内