板坯连铸结晶器内保护渣模拟方法地研究.pdfVIP

板坯连铸结晶器内保护渣模拟方法的研究 1 1 1 2 2 2 薛伟锋 文光华 唐 萍 何宇明 陈文满 赵正平 1.重庆大学材料科学与工程学院 重庆 400044 2.重庆钢铁股份有限公司炼钢厂 重庆 400084 摘 要 本文以重钢板坯连铸结晶器为研究对象 选用不同液面保护渣模拟材料进行实验 并结合实际生产结晶器内保护渣覆盖状况观察结 果 得出水模实验过程中合理的液面保护渣模拟方法 在此基础上建立起结晶器内液面波动大小与保护渣覆盖状况的关系 结果表明在实 际操作中结晶器内液面波动在3 7mm 范围内 可得到比较理想的保护渣覆盖效果 关键词 板坯连铸 保护渣覆盖 液面波动 物理模拟 Study on Simulation Methods about Fluxes in Slab Continuous Casting Mold 1 1 1 2 2 2 Xue Weifeng , Wen Guanghua , Tang Ping , He Yuming , Chen Wenman , Zhao Zhengping (1.College of Materials Science and Engineering, Chongqing University, Chongqing 400044; 2.Steelmaking Plant of Chongqing Iron Steel Co., Ltd., Chongqing 400084, China) Abstract In the paper, a reasonable methods of simulating fluxes on mold level is presented by the water modeling experiment for the slab caster at Chonggang. The different materials in the water model were employed to simulate fluxes on the level and the covered situation of fluxes was observed compared with the mold in the factory. The relationship between level disturbance and fluxes cover situation was obtained. The result showed that the situation of fluxes cover was perfect when the level disturbance was controlled within 3 7mm in the operational process. Keywords slab continuous caster, fluxes cover, level disturbance, physical modeling 1前言 实际生产中研究结晶器内钢水液面波动及保护渣覆盖情况比较困难 目前大多采用实验室物理 模拟的方法 对于结晶器内流场物理模拟 其主要目的就是优化得出最佳水口结构尺寸和浇注工艺 参数 保护渣模拟及液面波动实验正是衡量水口参数是否合理的一个重要方法 雷洪 齐新霞等人 都进行过这方面研究[1]-[2] 雷洪在实验中利用油来模拟液面保护渣覆盖状况 而齐新霞等在板坯结 晶器内卷渣现象研究的过程中 采用发泡塑料粒子模拟结晶器液面保护渣的卷入 两种方法均不能 正确反映实际中液面保护渣的覆盖情况 为了得到正确 可靠的实验结果 本文以重钢板坯连铸结 晶器为研究对象 选用不同液面保护渣模拟材料的方法进行实验 并与实际生产结晶器内保护渣覆 盖状况观察结果结合起来 得出水模实验过程中合理的液面保护渣模拟方法 建立起结晶器内液面 波动大小与保护渣覆盖状况的关系 确定合理的液面波动范围 给出液面波动控制措施 2