Cu含量对无取向硅钢热轧板织构影响.pdfVIP

·138· 2012年第十二届中国电工钢学术年会论文集 Cu含量对无取向硅钢热轧板织构的影响 黄希1”，项 利2，仇圣桃2，宋志国1 含量的增加，其热轧板表层织构混乱度增加，织构强度随着cu含量的增加其强度逐渐减少。但其织构种类并未发生 011。 关键词：无取向电工钢；织构；表面偏聚；Cu CuContentontheHot TextureofNon——orientedElectricalSteel Rolling HuangXil…，XiangLi2，QiuShengTa02，Songzhigu01 ofMaterialsScienceand ofScienceand (1．School Engineering，KunmingUniversity Technology， ResearchCenterofContinuous Kunming650093，Yunnan，China；2．NationalEngineering Casting CentralIronandSteelResearch 10008 Institute，Beijing1，China) ofEBSD thesimulationofCSP withCunon—orientedelectricalsteel Abstract：Usingtechnology，studied process textureevolution．WiththeincreaseofCu hot—roiledsurfacetextureconfusionin— strip content，the plate degree texture withtheincreaseofCucontent decreasedits thetexturehas creased，theintensity gradually strength．But types not main of1 10／／TDtexturetextures．In1／4and1／2 di— much．the 10／／ND．1 changed variety totheCuelement and texturehasnot rection，due segregationprecipitationeffect，thetypes changedmuch，the textureforthecubictexture cubetexture． of{100}001and{100}Ol types 1rotating electrical words：Non—oriented Key steel；Texture；copper 电工钢主要用于电动机和发电机的铁心材料，是国民生产和生活中不可缺少的一种重要的金属软磁材料。 数、夹杂物及析出物尺寸外，还受晶粒尺寸和织构的影响，并且最终退火板的晶粒尺寸和织构对最终磁性能的 的表面迁移。但是对于cu对无取向电工钢热轧板织构的研究暂时还没有发现相关的文献报道。笔者通过对 Cu含量对无取向硅钢热轧板织构的影响