AP1000 型压水堆核电站主管道焊接施工逻辑分析 杨青云 吴勇 刘先文 （中电投电力工程有限公司，上海 200233） Construction Logic Analysis of Welding AP1000 PWR Primary Pipe Yangqingyun, Wuyong, Liuxianwen (CPI POWER ENGINEERING CO.,LTD., ShangHai, 200233) Abstract: The AP1000 primary pipe welding is large AP1000 型压水堆核电站作为先进非能动型 diameter and thickness wrought austenitic stainless 压水堆核电技术的最大特点是设计简练，体 steel pipe welding, by means of ensureing the quality 现在主管道中是一个环路有3个整体锻造部 of the groove machining and assembly, determining 件、6 道焊缝，高品质的不锈钢锻造母材与 [1] the welding shrinkage data by welding process 精简的焊缝数量，降低了小破口失水事故 test/welding procedure qualification, and according to 的发生概率。在运行期间，LBB （破前先漏 the deformation direction for welding shrinkage of the 检测）技术的运用，对主管道大破口泄漏进 welding process, to avoid the excessive macroscopic 行了有效的控制。建设期的质量，就是运行 stress concentration. Through the comprehensive 期间的安全。在主管道安装焊接过程中，运 analysis of the three kinds of primary pipe welding 用焊接收缩变形的客观规律，控制宏观焊接 construction method including the sequence welding 应力的集中，提高主管道在运行期间不产生 construction, the cross multiplication construction and 小破口泄漏的可靠性。 the design of welded construction, in order to determine the reasonable welding sequence. 1 AP1000 主管道 AP1000 核岛有两个主管道环路，主要功 Key words: The primary pipe welding ; 能是通过主泵提供动力，将经蒸汽发生器冷 Construction logic; Welding 却后的冷却剂输送到压力容器，对堆芯进行 shrinkage 冷却，主要尺寸参数见表一。主管道采用超 低碳控氮奥氏体不锈钢 （ASME SA-376 TP316LN）整体锻造、弯制而成，机械性能 [摘要]AP1000 主管道焊接是大厚壁锻造奥氏体不 见表二。 锈钢管道焊接，在保证坡口加工与组对质量的同 表一 主管道参数 时，通过有效利用焊接工艺试验/焊接工艺评定确 名称 参数 定焊接收缩数据，按照变形的方向预留焊接收缩 主管道热段尺寸 Φ952.5×82.6 （mm） 量，通过焊接过程的自由收缩，避免宏观应力集中。