毕业设计（论文）-攀枝花铁精矿直接还原影响因素研究.doc

攀枝花铁精矿直接还原影响因素研究 摘 要 以攀枝花铁精矿为原料、煤粉作还原剂、D1和D2作联合催化剂，研究还原温度、还原时间、配碳量、催化剂以及各因素之间交互作用对冷固球团直接还原工艺的影响。采用五元二次回归正交设计试验，对试验结果回归出了金属化率、碳失重率及失氧率与各因素间关系，发现各单因素及因素之间交互作用对直接还原均有影响，尤其是两种催化剂的交互作用对金属化率的影响较大，经过优化试验得到温度在1280℃左右，时间在30min左右，配碳量在22.7%左右，催化剂D1加入量在2.5%左右，催化剂D2加入量在0.5%左右，其金属化率可达到95.54%ABSTRACT This paper studied the influence of factors about reducing temperature、reducing time、carbon quantity and catalyst as well as the interaction between the factors in which directing reduce iron concentrate of Pan zhihua with powdered coal as reducing agent and e D1 and the D2 as union catalyst. Using the regression orthogonal design to arrange the experiments,and getting the relationship of the metallization rate,the carbon lost rate and the oxygen lost rate with the factors ,and concluding that the single factor and the interaction between the factors are all have impact to the direct reduction, especially the interaction between the two catalysts have an important impact to the metallization rate. After optimized experiments, when the reducing temperature is about 1280 ℃,the reducing time is about 30 minutes, the carbon quantity is about 22.7 percent ,the content of the D1 is about 2.5 percent, and the content of D2 is about 0.5 percent, its metallization rate might achieve 95.54%,of course,there has not presented the phenomenon which the pellets are collapsed in the testing process. Key words Panzhihua Iron Concentrate,direct reduction, regression orthogonal design, pellet  目 录 摘 要 I ABSTRACT II 1 绪论 1 1.1 课题研究背景 1 1.2 主要直接还原方法 1 1.2.1 气基直接还原 1 1.2.2 煤基直接还原 2 1.3 直接还原发展状况 2 1.3.1 国内外发展概况 2 1.3.2 直接还原优势 3 1.3.3 存在问题 3 1.4 课题研究意义 4 1.5 课题研究目的 4 2 基本原理 6 2.1 还原剂的选择 6 2.2 铁氧化物还原特点 6 2.3 影响因素 8 2.3.1 还原温度 8 2.3.2 还原时间 10 2.3.3 配碳量 10 2.3.4 催化剂作用机理 10 3 试验内容 11 3.1 试验设备 11 3.1.1 试验设备 11 3.1.2 化验设备 12 3.2 试验原料 12 3.3 工艺流程 13 3.4 试验方案设计 13 3.5 试验过程 14 3.5.1 试验基本步骤 14 3.5.2 球团的压制 15 3.5.4 制样 15 4 试验结果及数据分析 16 4.1 试验结果 16 4.2 数据处理 16 4.2.1 方程回归 16 4.2.2 数据分析 18 4.3 验证试验 18 4.3.1 验证试