旋转闪蒸干燥生产拟薄水铝石 李广战 （中国铝业山东分公司，山东淄博 255052 ） 摘要：以车间生产的大孔拟薄水铝石为原料，进行不同操作条件下的闪蒸干燥试验，控制不同的进风及出风温度， o o 得到的试验样品指标有明显的差异。试验证明，采用进风温度 300 C，出风温度 110~120 C，能够生产出合格的 拟薄水铝石产品。使用闪蒸干燥省去了粉碎过程、节约了生产空间，因此该项目具有重大的实际意义。目前，生 产车间特种拟薄水铝石的设计已经采用该装备。 通过生产调试和运行，该设备已能完全满足普通拟薄水铝石和 大孔拟薄水铝石的烘干需要。 关键词：冶金技术；拟薄水铝石；闪蒸干燥器 Application of Spin Flash Drier in Manufacture of Pseudo-boehmite LI Guangzhan （Shandong Branch of CHALCO, Zibo, Shandong, 255051, China ） Abstract : Using macroporous pseudo-boehmite as raw material, significant difference was appeared when changed the temperature of spin flash drier. Conforming product was manufactured in the case of 300℃ inlet air temperature and 110- 120℃ outlet air temperature. The use of spin flash drier has great significance because of this project saves crushing process and production space. The drier has been equipped in the workshop. Practice has proved the spin flash drier could completely satisfy the production requirements of ordinary pseudo-boehmite and macroporous pseudo-boehmite. Keywords : metallurgical technology, pseudo-boehmite, spin flash drier 特种拟薄水铝石产品，由于其性能的特殊性而受到重视。产品主要应用于石油炼制催化剂载体的原料， 不同的生产工艺和方法制备的拟薄水铝石原料虽然指标相差不大，但对于催化剂的活性、选择性影响不同。 中国铝业山东分公司已投产的拟薄水铝石生产线，其中包括5000t 特种拟薄水铝石，特种拟薄水铝石的大 孔、小孔设计采用了一条生产线，分别生产两种（或者几种，因为大孔拟薄水的品种设定为两种）产品， 这样可以节约设备投资和生产空间，利于车间布置。 针对拟薄水铝石的洗涤，进行了带式过滤机的试验，结果不是很理想，主要原因是带式过滤机短，对 产品的洗涤不利，固尔沿用了压滤机。压滤机的分离过程采用了特殊的滤板，带静洗功能，这对特种拟薄 水铝石的洗涤是具有积极作用的。 大孔拟薄水的干燥，最初采用的是盘式干燥器，小孔采用了强化干燥器，盘式干燥的产能低。而旋转 闪蒸干燥设备，适合于膏糊状物料的干燥，而且产能高，另外还可以省去产品的粉碎过程。旋转闪蒸干燥 [1] [2] 器已成功应用于载体氧化铝 及洗涤剂用4A 沸石 的生产中，但是，采用该设备是否会对大孔拟薄水的