聚乙烯%2f层状双氢氧化物纳米复合材料热稳定增强机理研究.pdfVIP

聚乙烯/层状双氢氧化物纳米复合材料的热稳定增强机理研 究 邱龙臻，瞿保钧 火灾科学国家重点实验室，高分子科学与工程系，中国科学技术大学，合肥 230026 关键词： 层状双氢氧化物/聚乙烯纳米复合材料，热稳定性机理 Study of enhanced thermal stability mechanism of polyethylene/layered double hydroxides nanocomposites Longzhen Qiu, Baojun Qu State Key Laboratory of Fire Science and Department of Polymer Science and Engineering, University of Science and Technology of China, Hefei, Anhui 230026, Abstract The enhanced thermal stabilization mechanism of polyethylene/layered double hydroxides (PE/LDH) nanocomposites was studied by isoconversional kinetic analysis and dynamic FTIR spectroscopy capered with polyethylene/montmorillonite (PE/MMT) nanocomposites. Though both MMT and LDHs can enhance the thermal stability of PE due to the barrier effect, the LDHs can more effectively enhance the thermal stability of PE than MMT, because the PE/LDH nanocomposites can sharply increase the activation energy of degradation at the early stage of degradation due to the absence of catalysis dehydrogenation effect in PE/MMT. Keyword PE/LDH nanocomposite, enhanced thermal stability mechanism 近年来，聚合物/层状无机物纳米复合材料的制备与性能研究引起了人们的广泛关 注。与传统的复合材料相比，这种纳米复合材料具有优异的力学性能、阻隔性能、 热稳定性、抗溶剂腐蚀性和阻燃性能等。过去的研究主要集中在聚合物/层状硅酸 盐纳米复合材料上。相对而言，层状双氢氧化物(LDHs)却很少用于制备聚合物/层 状化合物纳米复合材料。对于聚合物/层状双氢氧化物纳米复合材料热稳定性提高 机理的研究更是鲜有报道。在这篇文章中，我们通过溶液插层法制备了蒙脱土（MMT NC）、镁铝层状双氢氧化物（MgAl NC）和锌铝层状双氢氧化物（ZnAl NC）的聚乙 烯纳米复合材料。应用非等温热分析和动态红外的方法系统研究了聚乙烯/层状双 氢氧化物纳米复合材料热稳定性增强机理。 图 1 是三种纳米复合材料20%失重时的温度随与无机片层含量的关系。可以看到 在相同无机片层含量时MgAl NC 还是ZnAl NC 的热降解温度比MMT NC 提高了9-40 oC。图二给出了无机片层含量为10%的三种纳米复合材料和聚乙烯在热降解过程中 表观活化能的变化。可以看到降解过程中聚乙烯的活化能始终保持在 70-103 kJ·mol-1 之间。在降解初期(α=0.03) ，三种纳米复合材料的热降解活化能与聚乙烯 相近。在那之后，MMT NC 的热降解活化能逐渐上升到220 kJ·mol-1 ；而MgAl NC 和 ZnAl NC 的表观活化能却在失重为α=0.1-0.2 时迅速升到227 和310 kJ·mol-1 ，之后 它们都有不同程度的下降。根据文献报道[1]，聚乙烯在有氧条件下降解的表观活 化能为70-110 kJ·mol-1 ，在惰性气体中降解的表观活化能