高阻尼TNCH合金的相变和阻尼性能研究.pdfVIP

第十二届全国青年材料科学技术研讨会（2009年11 月27-30） 3 有色金属材料 高阻尼 TNCH 合金的相变与阻尼性能研究 罗媛媛，赵永庆，候智敏，李倩 ( 西北有色金属研究院，陕西 西安 710016) 摘 要：研究了新型阻尼合金的马氏体相变、内耗以及它们之间的关系。结果表明：在室温低频范围 内合金主要经历了三个阶段：低温马氏体状态两相共存状态与母相状态。低温马氏体时，TNCH 合金 的高阻尼主要由B19＇马氏体变体、孪晶界面产生。相变过程中的阻尼特性与相变时新相/ 旧相的相界 面数量有关。合金处于母相时其阻尼主要来源于合金的晶体缺陷。 关键词：内耗；应变振幅；马氏体相变；振动频率 Damping properties of TNCH titanium alloy utilizing transformation Luo Yuanyuan,Zhao Yongqing, Hou Zhimin, Li Qian （Northwest Institute for Nonferrous Metal Research, Xi’an 710016 ) Abstract: The martensitic transformation and the internal friction was investigated for TNCH titanium alloy by using the X-ray diffraction, the scanning calorimeter (DSC) and dynamic mechanical analyzer( DMA) , as well as the relationship between them. The results showed that the TNCH alloys in the low-frequency range at room temperature had gone through three stages: low-temperature martensite, two-phase coexistence state and the mother phase state. First, the high damping properties of TNCH alloy were mainly induced by monoclinic martensitic phase (B19 )and twin interface. The second is that the damping characteristics during the phase ＇ transformation is concerned with the quantity of phase interface in new / old phase. The damping properties originated from the crystal dislocation when the alloy was in mother phase state. Key Words: internal friction; strain amplitude; martensitic transformation; frequency 1 引言 阻尼是材料的三大功能特性（超塑性、阻尼特性和形状记忆特性）之一。材料阻尼也 称内耗，通常是指材料将机械动能转化为热能而耗散于材料和环境中的现象[1] 。传统的阻尼 合金分为复相型 （如Zn-Al ）、铁磁型 （如Fe-Cr-Al ），孪晶型 （如Mn-Cu ）及位错型 （如Mg-Zr ）。 目前得到广泛关注的是Ti-Ni基合金与Cu基为代表的孪晶型高阻尼材料[2]，该类合金中的热 弹性马氏体表现出优异的减振能力，这比传统的结构金属材料要高至少一个数量级。TiNiCu 合金就是在TiNi合金基础上发展起来的一种新型形状记忆合金，由于具有小的相变滞后和宽 的使用温区而受到普遍关注[3～5] ，其中Ti50Ni25Cu25合金的阻尼性能尤为突出。 TNCH合金是Ti50Ni25Cu25合金合金基础上添加了微量的Y来替代Ni 的高阻尼合金，其 名义成分为Ti5