不同温升率下预载AZ31镁合金失效温度实验研究.pdfVIP

B78 不同温升率下预载 AZ31 镁合金失效温度的实验研究 陈斌 罗吉 袁权 （重庆大学资源及环境科学学院，重庆 400044） 摘要：使用Gleeble 1500热力模拟实验系统，研究了AZ31 镁合金试件在不同预载应力及不同温升率下的响应与 破坏规律。结果表明，随着预载应力或者温升率的增加，试样的失效温度相应降低。结合试件断口附近的金相显 微组织观察，表明高的温升率会导致严重的局部热失配，它将显著增加材料的微观缺陷和降低材料的宏观力学性 能。 关键词：AZ31镁合金；预载；温升率；失效温度；局部热失配 Effect of heating-rate on failure temperature of pre-loaded magnesium alloy AZ31 B Chen ，J Luo ，Q Yuan College of Resources and Environmental Science, Chongqing University, Chongqing, 400044, China Abstract: The response and failure of magnesium alloy AZ31 specimens subjected to different pre-loaded-stress levels and heating rates were investigated with a Gleeble-1500 thermal-mechanical material testing system. It was found that the increases of either pre-loaded stresses or heating-rates decrease the failure temperatures of the specimens. The metallographs of the tested specimens were also observed. It showed that the high heating-rate may cause stronger local thermal inconsistency, which remarkably increases the microdefects in the material and reduce the macroscopic mechanical properties of the material. Keywords: Magnesium alloy AZ31, pre-loaded stress, heating rate, failure temperature, local thermal inconsistency 引言 高温和快速升温会导致材料微结构变化[1-3]。微结构的变化将改变材料的力学性能。进行高温和快速升 温对材料微结构和力学性能影响的研究，将有助于避免材料在高温和快速升温情况下的失效，同时也有助 于提高快速升温下的材料加工技术[4-6]。 由高温和快速升温导致的材料和结构的失效，正受到人们日益地重视[7-10] [9] 。刘宗德等 对快速升温下铝 基金项目： 作者简介：陈斌，男，博士，教授，材料力学行为研究；bchen@cqu.edu.cn 合金的非线性热软化研究表明，不同的温升率历史会造成材料晶粒尺度和宏观力学性能的差异，并通过再 结晶动力学解释了这一现象。王春奎等[10]在采用快速加热方法获得不同温升率历史的 30CrMnSi 试件的拉 伸实验中发现，材料的断裂强度和金相显微