节镍型奥氏体不锈钢生产若干问题研究.pdfVIP

第二届钢材质量控制技术学术研讨会文集 节镍型奥氏体不锈钢生产的若干问题研究 季灯平，江来珠，吴狄峰 (宝山钢铁股份有限公司，上海，201900) 摘 要：研究了节镍型奥氏体不锈钢生产过程中的若干问题，主要包括：连铸板坯的组织及其在加热过程 的变化，形变马氏体的形成和消除规律，表面氧化皮结构受退火工艺的影响关系。根据研究结果， 制定了合理的生产工艺，生产出了高质量的节镍型奥氏体不锈钢冷轧带钢。 关键词：节镍型奥氏体不锈钢，生产 Research on several problems in production process of low nickel austenitic stainless steel JI Dengping, JIANG Laizhu, WU Difeng (Baoshan Iron and Steel Co., LTD, Shanghai, 201900) Abstract:： Several problems in production process of low nickel austenitic stainless steel are studied. These problems mainly include the microstructure of slabs and its evolution during heating process, the rule of formation and removal of deformation martensite, the relationship between the surface oxide structure and annealing process. According to the results, a reasonable manufacturing process is made, then high-quality cold rolled strips of low nickel austenitic stainless steel are produced. Key words:：low nickel austenitic stainless steel, produce 前言 节镍型奥氏体不锈钢是在传统304不锈钢的基础上，减少贵金属Ni的使用，添加Mn、N 等元素获得室温下单一奥氏体组织的经济型不锈钢。近年来，该类不锈钢以其优异的机械性 能和较好的耐腐蚀性能，受到不锈钢生产企业越来越多的关注，品种开发数量和产品产量均 呈逐年快速增长的趋势。然而，对于节镍型奥氏体不锈钢生产过程中的相关问题研究及其对 产品质量控制的影响，很少有文献公开报道。因此，研究和节镍型奥氏体不锈钢生产密切相 关的技术问题，为产品生产和质量控制提供科学的依据，具有十分重要的意义。 1 实验材料及方法 1.1 实验材料 实验用材料均为工业规模化生产的节镍型奥氏体不锈钢，其主要成分的范围如表1所示。 7 第二届钢材质量控制技术学术研讨会文集 表1 实验用节镍型奥氏体不锈钢的主要成分范围(%) Tab.1 Chemical composition of low nickel stainless steel in this study C Si Cr Mn Ni N Cu 0.15 1.0 14~17 6~10 0.5~4