节镍型奥氏体不锈钢紊流酸洗工艺与探讨.pdfVIP

节镍型奥氏体不锈钢紊流酸洗工艺探讨 ·1 · 节镍型奥氏体不锈钢紊流酸洗工艺探讨 郑其勇 祁卫东 林隆声 （宝钢不锈钢有限公司，上海 200431 ） 摘 要 目前世界上用于去除不锈钢表面氧化铁皮几乎都是采用浸没式酸洗技术，酸洗液为氢氟酸加硝酸。紊流酸 洗技术则多数被应用在普碳钢的酸洗且采用的酸洗液是盐酸，相比普通的浸没式酸洗紊流酸洗效率要高很多，本文 结合宝钢某紊流酸洗机组的生产情况，探讨采用氢氟酸加硝酸作为酸洗液的紊流酸洗技术去除节镍型奥氏体不锈钢 热轧表面氧化铁皮的工艺控制方法。 关键词 不锈钢 紊流酸洗 工艺控制 Discussion on Austenitic Stainless Steel of Turbulence Pickling Technology of Nickel Saving Zheng Qiyong Qi Weidong Lin Longsheng （Baosteel Stainless Steel Co., Ltd., Shanghai, 200431 ） Abstract At present the world used to remove the stainless steel surface oxidation iron is almost always used immersion pickling technology, acid liquid for hydrofluoric acid and nitric acid. Turbulence pickling technology is most used in acid pickling of carbon steel and the acid lotion is hydrochloric acid, and compared with the ordinary submerged turbulent pickling pickling efficiency is much higher, based on the baosteel pickling production a turbulent flow, explore the hydrofluoric acid and nitric acid as acid liquid turbulence pickling technology to remove section type nickel austenitic stainless steel hot rolling process control method of surface oxidation of iron. Key words stainless steel, turbulence pickling, process control 1 前言 酸洗是去除热轧不锈钢表面氧化铁皮的一道至关重要的工序，主要是通过酸洗液与带钢表面发生化学反 应和物理冲击使氧化铁皮从带钢表面脱落。从而形成较为理想的表面，以便带钢的后续加工做好准备。在酸 液的温度和浓度以及酸槽内流量一定的情况下，提高带钢与酸液接触面的传热效率是提高酸洗效率的最经济 有效的方法。节 Ni 含 N 的经济型奥氏体不锈钢，具有优异的力学性能，一定的耐蚀性，可以在弱腐蚀环境 下替代 304 不锈钢使用。它具有优异的力学性能；通过 N 合金化，相比 304 不锈钢具有更高的强度和几乎 相当的塑性，可以在同等承载能力需求下，起到产品的减重作用，节约材料和成本；可以通过合理的冷加工 和热处理工艺，获得具有高强度、高韧性的产品，满足特定用途的需求。 2 紊流酸洗工艺 宝钢某紊流酸洗机组主要设备有：焊机、抛丸机、中性盐回收系统、在线酸分析仪及氮氧化物处理系统 ·2 · 第九届中国钢铁年会论文集 等；采用浅槽紊流酸洗工艺，酸液（氢氟酸+硝酸）主要由设在每个酸槽两端的喷梁向带钢表面喷射，辅之 以由设在酸槽两侧的喷管向槽内喷酸，在槽内形成强烈的紊流状态，从