环保型氢氧化镁阻燃剂的制备的的研究.pdfVIP

第 32 卷第 2 期 2010 年 3 月 Vol. 32 No. 2 Journal of Tangshan Teachers College Mar. 2010 环保型氢氧化镁阻燃剂的制备研究 刘立华 （唐山师范学院化学系，河北 唐山 063000 ） 摘 要：氢氧化镁阻燃剂属于无机阻燃剂，具有热稳定性好、无毒、低烟、不产生腐蚀性气体、价格低廉等 优点，备受世界各国的青睐。本实验采用氨水法制备氢氧化镁无机阻燃剂，并通过实验讨论了初始反应温度和氨 镁摩尔浓度比对反应转化率的影响。实验结果表明：最佳初始温度为 20 ℃，氨镁摩尔浓度比为4:1 。 关键词：阻燃剂；氢氧化镁；制备；研究 TQ132.2 A 1009-9115(2010)02-0027-03 中图分类号： 文献标识码： 文章编号： Research on the Preparation of Green Flame Retardant of Magnesium Hydroxide LIU Li-hua (Department of Chemistry, Tangshan Teachers College, Tangshan 063000, China) Abstract: As inorganic flame retardant, magnesium hydroxide have advantages such as good heat steady, non-poisonous, low mist, no giving birth to gas with causticity, cheap and so on, it will be welcome by all the countries of the world. Ammonia method was adopted in the text. The effects on conversion of original reaction temperature and ratio of ammonia and magnesium were discussed in the paper. Experimental results showed that the best reaction temperature is 20 ℃, and ratio of ammonia and magnesium is 4:1. Key words: flame retardant; magnesium hydroxide; preparation; research 21 世纪是科技高速发展且环保的世纪，阻燃剂的开发 剂的 17%，其中有一半以上为三氧化二锑，而氢氧化铝和氢 [1] [3] 和应用也应向着环保型方向发展 。作为高效、低毒、无烟、 氧化镁还不到 10% 。我国阻燃剂的比例与世界发达国家和 无污染的无机阻燃剂的应用越来越广泛。发达国家阻燃剂消 地区相比，消费结构相差甚大，目前国外的阻燃剂已趋于无 费量大，其中无机阻燃剂占很大比重，且所占分额有上升趋 机阻燃剂为主，而我国还是以污染较大、毒性较高的卤系阻 势。发达国家和地区阻燃剂产品结构如表 1 所示。 燃剂为主。我国应不断加快无机阻燃剂的开发应用。 表1 发达国家和地区阻燃剂产品结