第 26 卷第 3 期 纺 　织 　学 　报 Vol . 26 ,No . 3 2005 年 6 月 Journal of Textile Research Jun . ,2005 添加碳纳米管聚酯母粒的制备及性能 钱建华 ,凌荣根 ,黄志超 ,程贞娟 (浙江理工大学 材料与纺织学院 , 浙江 杭州 　310033) 摘 　要 　采用扫描电镜及 X 射线衍射仪对碳纳米管进行了表征 。经表面改性后 ,与聚酯粉体共混造粒 、挤出。应 用近代测试方法对母粒的结构和性能进行了测试分析 ,给出了碳纳米管的含量与导电性能及可纺性之间的关系 。 关键词 　碳纳米管 ; 聚酯 ; 导电性 ; 可纺性 ( ) 中图分类号 :TQ 340 . 42 　　　文献标识码 :A 　　　文章编号 2005 Preparation and property of carbonnanotubesPET QIAN Jianhua , L IN G Ronggen , HUAN G Zhichao , CHEN G Zhenj uan ( College of M aterial and Textile , Zhej iang University of Science and Technology , Hangzhou , Zhej iang 　310033 , China) Abstract 　The microstructure of carbonnanotubes was charaterized by SEM and X diffration . After the surface modification ,CNTs was mixed with polyester powder and then been extruded and chipped. CNTspolyester property and the structure were tested with DSC ,conductibility and viscometer . The relation between CNTs content in PET and conductibility , spinnability was given . Key words 　carbonnanotubes ; polyester ; conductibility ; spinnability ( ) 　　碳纳米管 CNTs 是 1991 年 日本 NEC 公司的 法研制成导电性及可纺性优良的聚酯母粒 。 Iij ima 教授用电弧法制备 C60 时在阴极沉淀物中发 1 　实验部分 现的 ,这种中空管状物的直径只有 07～30 nm ,被称 作碳纳米管 。它具有优 良的电学和力学性能 ,其导 1. 1 　原 　料 电性能优于铜 ,它的模量是钢的 100 倍[ 1] 。同时 ,碳 CNTs :清华大学化工系生产 , 直径 30 ～40 nm , 长度 2 ～ 3 μ η为 纳米管还具有微波吸收性能 ,在工程材料的纳米增 m ; PET : 上 海 金 山石 化 生 产 , 强相 、半导体材料 、超导电性