火力发电厂凝汽器管腐蚀评价方法的研究.pdfVIP

电厂化学201I学术年会论文集 2011．10上海 火力发电厂凝汽器管腐蚀评价方法研究 张燕·．刘国强，许立国。宋丽莎，侯亚琴 山东电力研究院(山东济南250002) I摘要1分别采用失重法(静态旋转挂片法和动态模拟法)与电化学方法(极化曲线和线性极化电阻法)研究了三种常见凝汽 蚀速率略低于旋转挂片试验得到的腐蚀速率．电化学方法得到的腐蚀速率与失重法的结果基本一致． 1关键词I腐蚀评价失重法电化学 A onEvaluationMethodsofCondenserTubesatThermalPlant Study Yah Xu·Li—sha Hou Zhang。Guo-qiangLiu·Li·guo Song，Ya-qin Research 250002。Ch／na) Electric Institute，Jinan (Shandong ABSTRACTsRotation simulationtestandV：UIOU$electrochemical specimenmethod．dynamic methods，includingpolarization andlinear resistance toevaluatethecorrosionofthreecondensertubematerials curves polarizationmeasurement(LPR)wc他employed carbon brassand316Lstainless surfacewater．ResultsindicatethatthecorrosionratesofHSn70．1Bbrass (撑20 steel，HSn70-1B steel)in inthe watertreatedscale-corrosioninhibitorsand with and316LstainlessateelarebothIessthan0．005mm／a surface by acid concentrationratioof4。Theresultof simulationtestisalittlelessthanthatofrotation method。Thecorrosionrates dynamic specimen obtained andmaSSlossmeasurementare thesame． byelectrochemistry basically KEYWORDSt lOSS corrosion；evaluation；massmeasurement；electrochemistry 火力发电是我国取水量最大的行业之一，其中冷却用水占据相当人的比例。为做好发电机组水资源 利用优化，提高循环水系统节水水平，应提前做好循环冷却水系统的防腐、防垢工作。凝汽器是火电厂 热力系统的重要设备之一。凝汽器防腐蚀的意义不仅在于保护设备免于腐蚀，更重要的是避免冈凝汽器 腐蚀泄露而给锅炉机组正常运行带来隐患。凝汽器冷却管的腐蚀一直为设计、制造和运行人员所迫切关 注，是需高度防范的焦点问题。 本文分别采用静态旋转挂片法、动态模拟法和电化学方法研究了地表水做循环冷却水过程中常见凝 汽器管材的腐蚀情况，这对保证系统的安全运行及采取正确的维护手段，有着重要的指导意义。 l试验部分 1．1试验水质 试验用水采J{J山东某电厂当地的地表水，实验之前加入Smg／L复配阻垢缓蚀剂TL一559并辅助加酸。 水质见表l。