第33卷第4期 化工新型材料 V01．33No．4 2005年4月 NEWCHEMICALMATERIALS ·25· 丙酮对Ti—PILCs合成实验条件的影响 项茹强敏张一敏 (武汉科技大学化工与资源环境学院，武汉430081) 摘要 说明在Ti—P1LCs制备过程中，丙酮的加入对蒙脱土层间引入较大粒径的钛聚合羟基阳离子，促进钛 聚合羟基阳离子与钠离子交换是有利的。 关键词钠基蒙脱石，钛交联，复合材料，丙酮 Tlleeffectofacet蚰e蚰test conditionsofTi—PILCs synthesizing Ru Min Yimin XiangQiang Zhang (Wuhan ofScienceand 430081) University Technology，Wuhan Abstr舵t as themixture H9o)4 ti协i姗凇ource，Na—montmorilloniteasthe US诹Ti(n-C4 startingclay，and of、Ⅳaterandacetoneas were when Solvent，titallium-pillaredclays prepared were HCl=5mol／L．ThelIlate础scharacterized diffraction，N2 bypowerx_ray adsorption／deSorptionamlySes．The results of free and showed，whenV‰o：Vacetone一1：2，titaniun卜pillaredclayspossessedinterlayer3．37mspacing surfaceareaof its is2．3timesofthematerials谢thoutacetone．Italso specific 389．1m2倌，andproductivity adding the acetonecan thein— courseof titani眦cations showed，during preparing，addinghelpbigsizepolyhydroxy inserting ofNa—nlontnloriUoniteand withNa+． terlayer exchangd wOrds material，acetone Key Na．rnonnnorillonite，titaniumpillaring，composite 交联粘土材料作为一种新型的人工合成分子筛 蒙脱石为基质材料、钛酸丁酯为钛源，制备钛交联蒙 催化剂，具有规整的二维孔道结构，与一般的分子筛