Nd含量对快淬纳米晶和非晶(Mg24Ni10Cu2)100-xNdx(x=0~20)合金电化学性能的影响.pdfVIP

Nd含量对快淬纳米晶和非晶(Mg24Ni10Cu2)100-xNdx(x=0~20)合金电化学性能的影响.pdf

  1. 1、本文档共11页,可阅读全部内容。
  2. 2、原创力文档(book118)网站文档一经付费(服务费),不意味着购买了该文档的版权,仅供个人/单位学习、研究之用,不得用于商业用途,未经授权,严禁复制、发行、汇编、翻译或者网络传播等,侵权必究。
  3. 3、本站所有内容均由合作方或网友上传,本站不对文档的完整性、权威性及其观点立场正确性做任何保证或承诺!文档内容仅供研究参考,付费前请自行鉴别。如您付费,意味着您自己接受本站规则且自行承担风险,本站不退款、不进行额外附加服务;查看《如何避免下载的几个坑》。如果您已付费下载过本站文档,您可以点击 这里二次下载
  4. 4、如文档侵犯商业秘密、侵犯著作权、侵犯人身权等,请点击“版权申诉”(推荐),也可以打举报电话:400-050-0827(电话支持时间:9:00-18:30)。
  5. 5、该文档为VIP文档,如果想要下载,成为VIP会员后,下载免费。
  6. 6、成为VIP后,下载本文档将扣除1次下载权益。下载后,不支持退款、换文档。如有疑问请联系我们
  7. 7、成为VIP后,您将拥有八大权益,权益包括:VIP文档下载权益、阅读免打扰、文档格式转换、高级专利检索、专属身份标志、高级客服、多端互通、版权登记。
  8. 8、VIP文档为合作方或网友上传,每下载1次, 网站将根据用户上传文档的质量评分、类型等,对文档贡献者给予高额补贴、流量扶持。如果你也想贡献VIP文档。上传文档
查看更多
Nd含量对快淬纳米晶和非晶(Mg24Ni10Cu2)100-xNdx(x=0~20)合金电化学性能的影响.pdf

Trans. Nonferrous Met. Soc. China 23(2013) 3668−3676 Effect of Nd content on electrochemical performances of nanocrystalline and amorphous (Mg Ni Cu ) Nd (x=0−20) alloys prepared by melt spinning 24 10 2 100−x x 1,2 2 1,2 1 1 2 Yang-huan ZHANG , Tai YANG , Wen-gang BU , Ying CAI , Guo-fang ZHANG , Dong-liang ZHAO 1. Key Laboratory of Integrated Exploitation of Baiyun Obo Multi-Metal Resources, Inner Mongolia University of Science and Technology, Baotou 014010, China; 2. Department of Functional Material Research, Central Iron and Steel Research Institute, Beijing 100081, China Received 12 September 2013; accepted 21 October 2013 Abstract: The nanocrystalline and amorphous Mg Ni-type alloys with a chemical composition of (Mg Ni Cu ) Nd (x=0, 5, 10, 2 24 10 2 100−x x 15, 20) were fabricated by melt spinning technology. The effects of spinning rate on the structure and electrochemical hydrogen storage performance of the alloys were investigated. The as-spun Nd-free alloy displays an entire nanocrystalline structure, whereas the as-spun Nd-added alloys hold a nanocrystalline and amorphous structure, suggesting that the addition of Nd facilitates the glass forming of the Mg2Ni-type alloys. Increasing the spinning rate from 0 to 40 m/s gives rise to the discharge capacity growing from 42.5 to 100.6 mA·h/g for the x=0 alloy and from 86.4 to 452.8 mA·h/g for the x=10 alloy. And th