微米级薄片木纤维高强度人造板制造工艺的试验研究.pdfVIP

研究与设计 2006 年第1 期 微米级薄片木纤维高强度人造板 制造工艺的试验研究 阿伦，马岩，战丽，许彦博，杨春梅，孟庆军 ( 东北林业大学林业与木工机械工程技术中心，哈尔滨 150040 ) 摘要：利用微米级长木纤维在实验室成功地压制了人造板，初步验证了微米级木纤维形成高强度纤维板 (MFB) 的细胞裂解理论。试验结果表明这种板材外观呈现木本色，在某些物理力学性能上 (MOR ，MOE ， 握钉力等) 优于MDF 和B 类刨花板。 关键词：微米；木纤维； MFB ；试验 中图分类号：TS653 文献标识码：A 文章编号：1001-036X(2006)01-0022-03 Study of processing MFB with wood micro-fiber A Lun, MA Yan, ZHAN Li, XU Yan-bo, YANG Chun-mei, MENG Qing-jun ( Forestry Wood Mechanical Engineering Technology Center of Northeast Forestry University, Harbin 150040, China ) Abstract: This paper focused on a new wood-based panelMFB, which was pressed with wood micro-fiber, proved the cell break theory of using wood fiber micro-meter reconsolidated technology forming super high-strength wood-based panel successfully in the laboratory, and also made a comparison of physical and mechanical properties among particleboard of kind B, MDF, OSB, HDF, and MFB. The results showed that MFB is in wooden color and high strength. Key words: micrometer; wood-fiber; MFB; experiment 3 在纤维微米加工技术的研究中，通过改变木材 木材的细胞壁物质密度一般约为1.53g/cm , 但 3 细胞的劈裂方式，在加工过程中可以清除木材的几 木材的整体密度一般小于1g/cm 。在纳微米技术发 乎所有天然缺陷，剔除降低强度的其它有缺陷纤维 展的今天，微米木纤维的加工和重组技术，可以获得 [1] 组织 。为了开发具有自主知识产权的人造板，利用 完全没有缺陷的木纤维，在近似纯木纤维的条件下， 微米纤维重组理论，提出一种新型的人造板“微米 在理论上可以制造出强度高、密度大的新板种 级薄片状纤维高强度人造板”简称：微纤板，英文 MFB ，而且这种板材的很多性能完全可能超出传统 [2]