The process of electroplating with Cu on the surface of Mg–Li alloy.pdf
Surface Coatings Technology 225 (2013) 119–125
Contents lists available at SciVerse ScienceDirect
Surface Coatings Technology
journal homepage : www. elsevi er. com/ locate/ surfcoat
The process of electroplating with Cu on the surface of Mg–Li alloy
Tingting Yin, Ruizhi Wu ⁎, Zhe Leng, Guanjun Du, Xuying Guo, Milin Zhang, Jinghuai Zhang
Key Laboratory of Superlight Materials Surface Technology, Ministry of Education, Harbin Engineering University, Harbin 150001, PR China
a r t i c l e i n f o a b s t r a c t
Article history: Mg–Li alloy is a potential applied material because of its ultra-low density. Its poor corrosion and wear resis-
Received 20 July 2012 tance hinder the expansive applications. In this research, an electroplating mean was carried to obtain a
Accepted in revised form 15 March 2013 Cu-coating on the Mg–Li alloy. The main factors that influence the electroplating effect were examined
Available online 26 March 2013
through orthogonal experiments, and the determined optimum processing parameters by electrochemical
tests are as follows: concentration of main salt is 50 g/L, current density is 2 A/dm2, solution temperature
Keywords:
is 40 °C and electroplating time is 30 min, respectively. Afterwards, surface and cross-section morphology
Mg–Li alloy
Electroplating feature and elemental composition were characterized by SEM and E
您可能关注的文档
- Simulink模块库.pdf
- SKODA品牌文化.ppt
- skriptum_kap2,4.pdf
- SL高低配豪宅产品启动模式案例1132345989-.ppt
- Spatially resolved in situ strain measurements from an interior twinned grain in bulk polycrystalline AZ31 alloy.pdf
- Springback characteristics of AZ31 magnesium alloy as-extruded profile in warm tension-rotation bending process.pdf
- Spring_b.ppt
- Sr,Y对AZ31镁合金显微组织与力学性能的影响.pdf
- Stabilization of metastable phases in Mg–Li alloys.pdf
- Static recrystallization behavior of hot-deformed magnesium alloy AZ31 during isothermal annealing.pdf
- 《GB/T 12668.7202-2024调速电气传动系统 第7-202部分:电气传动系统的通用接口和使用规范 2型规范说明》.pdf
- 《GB/T 15692-2024制药机械 术语》.pdf
- GB/T 15692-2024制药机械 术语.pdf
- 中国国家标准 GB/T 15692-2024制药机械 术语.pdf
- GB/T 19633.1-2024最终灭菌医疗器械包装 第1部分:材料、无菌屏障系统和包装系统的要求.pdf
- 中国国家标准 GB/T 19633.1-2024最终灭菌医疗器械包装 第1部分:材料、无菌屏障系统和包装系统的要求.pdf
- 《GB/T 19633.1-2024最终灭菌医疗器械包装 第1部分:材料、无菌屏障系统和包装系统的要求》.pdf
- 《GB/T 30117.1-2024非相干光产品的光生物安全 第1部分:通用要求》.pdf
- 《GB/T 33348-2024高压直流输电用电压源换流器阀 电气试验》.pdf
- GB/T 33348-2024高压直流输电用电压源换流器阀 电气试验.pdf
文档评论(0)