一种高强度铝合金焊接结构的开裂分析 隋显庭，金文涛，云中煌 （南车南京浦镇车辆有限公司，江苏南京 210031 ） 摘要：轨道车辆铝合金焊接结构失效一直是焊接结构的重大问题。本文针对一种高强度铝合金焊接结构在焊接加 工完成后开裂进行原因分析，通过对其化学成分、机械性能、晶粒度、组焊工艺等方面分析找到此结构开裂的根 本原因，并通过大量实验进行验证，通过优化焊接工艺手段、控制焊接变形、焊后残余应力消除等手段制定相应 的预防措施，使产品结构稳定、可靠。 关键词：轨道车辆；铝合金；焊接结构失效 Analysis on Cracking of A Kind of High-strength Aluminum Alloy Welding Structure With SUI Xianting, JIN Wentao, YUN Zhonghuang （CSR Nanjing Puzhen Co., Ltd., Nanjing 210031, China ） Abstract: Aluminum welded rail vehicles has been a major problem of structural failure of welded structures, this paper focused on a high-strength aluminum alloy welded structure after the completion of welding crack cause analysis, by its chemical composition, mechanical properties, grain size, group welding technology and other aspects of the analysis to find the root cause of this structural cracking, and by a large number of experiments to verify, by optimizing the welding process means to control the welding deformation after welding residual stress relief and other means to develop appropriate preventive measures to make the product stable and reliable structure. Keywords: rail vehicles, Aluminum, failure of welded structures 1 前言 一种高强度铝合金焊接结构在焊接加工完成后，在热影响区产生母材开裂现象，裂纹形貌呈沿着母材 挤压成型的纤维流线方向延伸，裂纹与圆弧所在平面呈30°左右夹角向外延伸，裂纹深度最大处4mm （图 1）。 作者简介：隋显庭，联系电话E-mail ：suixianting@126.com 1 图1 裂纹形貌 2 原因分析 鉴于此种结构是一种成熟的焊接结构，具有实际应用经验，且应用过程中无裂纹产生，故从材料本身、 生产工艺、模拟仿真3 方面进行原因分析。 2.1 化学成分分析 对产生裂纹的母材选择同一批次号进行化学成分分析，分析结果见表1 所示，均符合JIS H4100 标准 中A7N01S-T5 的化学元素成分要求。 表1 化学成分分析结果 牌号 Si Fe Cu Mn