皖 西 学 院 本科毕业论文（设计）  论 文 题 目 姓名（学号） 系 别 专 业 化学 导 师 姓 名 （教授） 二0年五月 摘要: 通过分子印迹技术，以2,4-D为模板分子丙烯酰胺(AM)为功能单体Fe3O4磁性纳米微球制备具有特异性识别的磁性分子印迹聚合物通过紫外分光光度法对磁性印迹聚合物的吸附性能进行研究，并对吸附特性进行了探讨利用等温吸附数据进行Scatchard分析从而推断出印迹聚合物的最大吸附量Qmax为280.99 mol/g，平衡离解常数KD为1.58×103 mol/L，分析印迹聚合物的结合机理和动态吸附特征结果表明制备的磁性分子印迹微球对模板分子存在较高的吸附特异性关键词：Fe3O4磁性纳米微球分子印迹聚合物吸附特性 AbstractMagnetic molecularly imprinted polymer was prepared by using 2,4-D as template molecule，MAA as functional monomer and Fe3O4 magnetic fluid. The Fe3O4 magnetic fluid was successful preparedly by chemical hydrothermal method. The recognition mechanism of polymer was studied by UV spectrophotometry. The adsorption properties and selectivity ability were analyzed by Scatchard analysis and the equilibrium rebinding experiments. The results clearly exhibit that the synthesized magnetic molecularly-imprinted polymers have high binding ability. Scatchard linear regression analysis indicated that the apparent maximum binding capacity (Qmax) was 280.99 mol/g and the dissociation contents (KD) was 1.58×10-3. Keywords ： Fe3O4 magnetic nanoparticles; molecular imprinting polymers; absorption characteristic 1前言 分子印迹聚合物[1] (molecular imprintingolymers, MIPs)是一种对目标分子具有特异选择性和识别能力的高分子功能材料相对于生物抗体MIPs对印迹分子及其结构类似的客体分子具有特异结合和识别性且具有较好的物理和化学稳定性成本低易制备在色谱分离仿生传感器[]、 [5]、固相萃取[]等许多领域都具有良好的应用前景而Fe3O4磁性纳米粒子[] 、 [7]的特殊磁导向性超顺磁性及表面可连接生化活性功能基团等特性，使其在核酸分析临床诊断靶向药物[]、酶和细胞固定化等领域的应用得到了广泛的发展球使其兼具良好的超顺磁性和高选择吸附性两大优点将进一步拓展分子印迹与磁性微球的应用对农残的检测起到一定的推动作用本文以2,4-D为模板分子，利用悬浮聚合法制备磁性分子印迹聚合物[]，对其识别机理和结合特性进行研究，期望得到良好的印迹效果，从而提高其分离分析的速度和准确性实验部分 2.1 实验仪器 WQF-310傅立叶变换红外光谱仪（北京第二光学仪器厂）；FA-1604电子天平，精密度0.1mg（上海精科天平）；半微量有机制备仪BB-26型（天长市千玻教学仪器有限公司）；DZF-6020型真空干燥箱（上海福玛试验设备有限公司）；聚四氟乙烯衬里釜（江苏省金坛市医疗仪器厂）集热式恒温加热磁力搅拌器( DF-101S)， 郑长城科贸有限公司; KQ-400KDE型高功率数控超声波清洗仪Q2200DB)， 昆山市超声仪器有限公司; HC-3578高速冷离心机（科大创新股份有限股份），IKA KS4000i control 恒温摇篮，GZX-9070 MBE 数显鼓风干燥箱（上海博讯实业有限公司医疗设备厂）。 2.2 实验试剂 六水合硫酸亚铁铵2, 2′-偶氮二异丁腈(A