电渣重熔过程中夹杂物的控制耿鑫.pdfVIP

第 44 卷 第 12期 钢 铁 Vol. 44, No. 12 2 0 0 9 年 12 月 Iron and Steel December 2009 , , , (东北大学材料与冶金学院, 辽宁 沈阳 110004) : 电渣重熔过程中非金属夹 物的去除主要发生在自耗电极端头熔滴形成期以及熔滴滴落穿过熔渣层阶 段。电渣重熔过程中原生夹 物去除的同时将产生新的夹 物, 为了有效地控制电渣锭中的夹 物, 使用复合脱 氧剂对自耗电极进行终脱氧, 采用合理的重熔速度、熔渣的化学组成和供电制度, 以及严格控制电渣炉内氧位。 : 电渣重熔; 夹 物; 动力学; 比接触面积 : TF744 : A : 04492 749 (2009) 122 00422 04 Control of Non2metallic Inclusion in ESR Process GENG in, JIANG Zhou2hua, LIU Fu2bin, LIANG Lian2ke ( School of Materials and Metallurgy, Northeastern University, Shenyang 110004, Liaoning, China) Abstract: The removal of non2metallic inclusion during remelting occurred mainly in stages of formation of dropets on the consumable electrode tip and dropets falling through the slag. The dynamics viewpoint of the lager Specific Contact Area can be used to discuss it. There will produce new inclusion with the removal of original inclusion. Therefore, to effectively control inclusions in ESR ingots, compound deoxidizer should beused as the final deoxidi2 zer, using reasonable remelting speed, composition of slag, power supply system and the oxygen potential in elec2 troslag furnace should be strictly controlled. Key words: ESR; non2metallic inclusion; dynamics; specific contact area [1~ 5] 大量的研究工作 指出, 电渣重熔的显著优 中, 自耗电极熔化成金属熔池过程可分为3个阶段, 点之一就是可显著降低电渣钢中非金属夹 物并改 如图1所示。第一阶段: 自耗电极端头在渣池中形 [1] 善其在钢中的分布 。在M. M. K½Ð¶³等人 的工 成熔滴;第二阶段: 脱落的熔滴穿过熔渣层; 第三阶 作中, 用AHÆ25、AHÆ26、AHÆ21‘和 AHÆ229 炉 段:熔滴形成金属熔池。 渣,对 š—15、š—15“T、ŸŠ961、ŸŠ481、—189、 ŸŠ847、ŸŠ851