2124铝合金疲劳裂纹扩展的EBSD分析英文蹇海根.pdfVIP

Rare Metal Materials and Engineering Volume 43, Issue 6, June 2014 Online English edition of the Chinese language journal Cite this article as: Rare Metal Materials and Engineering, 2014, 43(6): 1332-1336. ARTICLE EBSD Analysis of Fatigue Crack Growth of 2124 Aluminum Alloy for Aviation 1,2 2 2 2 Jian Haigen , Yin Zhimin , Jiang Feng , Li Xue 1 2 Hunan University of Technology, Zhuzhou 412007, China; Central South University, Changsha 410083, China Abstract: The fatigue crack growth of 2124-T851 aluminum alloy was investigated by Electron Backscatter Diffraction (EBSD) analysis. The result shows that the mode of fatigue crack growth is mainly transcrystalline, and the preferential orientation changes with the difference of grain orientation. When the crack extends to the grain boundary, the deflection of the crack against the normal extensive path will take place as a result of the misorientation of adjoining grains, but the deflection of the crack in the grain inner is mainly caused by the coarse second phase particles which are poor in coordination of deformability under cyclic stress. The phenomenon of bifurcation during the process of the crack propagation is relative with the specific crystallographic direction, which is caused by the simultaneous movement of numerous equivalent {111}110 slip system on crack-tip. Key words: 2124 aluminum alloy; fatigue crack growth; misorientation; electron backscatter diffraction In order to improve the fracture toughness of 2024 after aging treatment on 2024 aluminum alloy in different ti