《Micro-mechanism of metal magnetic memory signal variation during fatigue.》.pdf

InternationalJournalofMinerals，MetallurgyandMaterials Volume21，Number3，March2014，Page259 D01：10．1O071s12613-014-O903_z Micro-mechanism ofmetalmagneticmemorysignalvariationduringfatigue Ming-xiuXunZhang-huaChennandMin—qiangXu) ， ， 1)SchoolofMathematicsandPhysics，UniversityofScienceandTechnologyBeijing，Beijing100083，China 2)DivisionofVehicleDynamicsControl，HarbinInstituteofTechnoloyg，Hrabni150001，China (Received：25September2013；revised：28November2013；accpeted：29November2013) Abstract：Tensilefatiguetestsweredesignedtostudytherelationbetweenthetangentialmang eticmemo~ signalanddislocations．Accord． ingtoexperimentalresults，inhteearlysatgeoffatigue，htemagneticsignalandhtedislocationdensityrapidlynicrease；whileinhtemiddie satge，htema gneticsignalgraduallyincreases，htedislocationdensiytremainssteady，andonlyhtedislocationstructuredevelops．Onhte ohterhand，inhtelatersatge，themangeticsing alonceagainincreasesrapidly，htedislocationstructurecontinuestodevelop，andmicro— scopiccmcksraeformed．Analysisrevealsthathtedislocationsblockhtemovementofhtedomainwal1．andhteareaofdislocationaCCUlTIU． 1ationhtusbecomesna niternalmang eticsourceandscattersafieldouwt rad．Inaddition．htemang eticmemo~ fieldstrengthenswim in． Crewnigdislocationdensiyt nadcomplexiyt ofhtedislocationstructure．Accordingly，htedislocationpinningfactorrelatedwihthtedisloca- tiondensitynadhtedislocationstructurehasbeenproposedtocharacterizehteeffectofdislocationsonhtemang eticmemo~ singa1．The mang eticsingalsrtengthenswithanincreaseinhtedislocationpinningfactor． Keywords：fatiug eofmaterials；meatlmagneticmemo~；dislocations；mang eticfields tion-oriented studiesperformed on the M techn ique 1．Introduction havedemonstratedconstructiveresults 3『_41．Amonghtem， htede