《Forming technology of boiling structure on evaporation surface of phase-change heat sink for high-power light emitting diode》.pdfVIP

J. Cent. South Univ. Technol. (2010) 17: 544−548 DOI: 10.1007/s11771−010−0520−6 Forming technology of boiling structure on evaporation surface of phase-change heat sink for high-power light emitting diode XIANG Jian-hua( 向建化), YE Bang-yan(叶邦彦), TANG Yong(汤勇), ZHOU Wei(周伟), HU Zhi-hua(胡志华) School of Mechanical and Automotive Engineering, South China University of Technology, Guangzhou 510640, China © Central South University Press and Springer-Verlag Berlin Heidelberg 2010 Abstract: Boiling structures on evaporation surface of red copper sheet with a diameter (D) of 10 mm and a wall thickness (h) of 1 mm were processed by the ploughing-extrusion (P-E) processing method, which is one part of the phase-change heat sink for high power (HP) light emitting diode (LED). The experimental results show that two different structures of rectangular- and triangular-shaped micro-grooves are formed in P-E process. When P-E depth (a ), interval of helical grooves (d ) and rotation speed p p (n) are 0.12 mm, 0.2 mm and 100 r/min, respectively, the boiling structures of triangular-shaped grooves with the fin height of 0.15 mm that has good evaporation performance are obtained. The shapes of the boiling structures are restricted by d and a , and d p p p is determined by n and amount of feed (f ). The ploughing speed has an important influence on the formation of groove structure in P-E process. Key words: phase-change heat sink; boiling structure; high power light emitting diode; ploughing-extrusion