good材料现代分析测试方法射线衍射.ppt

Bragg-Brentano optics θ-θ连动 Sample surface bisects incident and scattered beams ? Scattered beam focus at the same distance as the tube focus Optimal resolution Conventional phase analysis 第6章 X射线多晶衍射仪的应用 物相定性分析 物相定量分析 结晶度分析 晶胞参数的精确测定 纳米晶粒尺寸分析 结构畸变分析 材料的残余应力分析 原位反应分析 未知结构的粉末结构解析 材料的织构分析 Peak list No. h k l d [A] 2Theta[deg] I [%] 1 0 1 2 3.46196 25.712 66.4 2 1 0 4 2.53713 35.349 100.0 3 1 1 0 2.36760 37.974 46.5 4 0 0 6 2.15293 41.929 0.4 5 1 1 3 2.07466 43.590 91.6 6 2 0 2 1.95429 46.427 1.5 7 0 2 4 1.73098 52.848 46.0 8 1 1 6 1.59285 57.841 88.1 9 2 1 1 1.53892 60.072 2.1 10 1 2 2 1.50717 61.473 3.2 11 0 1 8 1.50243 61.688 7.4 12 2 1 4 1.39735 66.907 33.9 13 3 0 0 1.36693 68.600 50.2 14 1 2 5 1.32911 70.839 1.0 15 2 0 8 1.26856 74.778 1.3 16 1 0 10 1.23208 77.394 14.2 17 1 1 9 1.22737 77.747 7.6 18 2 1 7 1.18686 80.936 0.7 19 2 2 0 1.18380 81.189 6.0 20 0 3 6 1.15399 83.750 0.9 21 2 2 3 1.14145 84.884 3.9 22 1 3 1 1.13298 85.670 0.2 23 3 1 2 1.12012 86.896 3.1 24 1 2 8 1.11817 87.085 2.9 25 0 2 10 1.09295 89.625 6.2 从线形增宽中获得晶粒尺寸及微观应力的信息，必须完成两项工作： 1）从B中扣除b，求β。 2）从β中再分离出m和n。 第一项工作可用式(B)完成，但需知道f(x)，而f(x)难以知晓。 当然可以根据式(A)，用实验得到的h(x)、g(x)线形数据，通过傅里叶反变换及去卷积过程，求出f(x)，但计算工作量相当大而繁。 （五）物理宽度分离的实际困难和方法 另一途径是直接假设各种宽化线形为某种已知函数，无须得知f(x)整个线形数据，通过B和b利用式（B）求出β。这就是“近似函数法”。 第二项工作，更难指望从f（x）中分离出M（x）和N（x），再求得相应的两个物理