- 1、本文档共5页,可阅读全部内容。
- 2、原创力文档(book118)网站文档一经付费(服务费),不意味着购买了该文档的版权,仅供个人/单位学习、研究之用,不得用于商业用途,未经授权,严禁复制、发行、汇编、翻译或者网络传播等,侵权必究。
- 3、本站所有内容均由合作方或网友上传,本站不对文档的完整性、权威性及其观点立场正确性做任何保证或承诺!文档内容仅供研究参考,付费前请自行鉴别。如您付费,意味着您自己接受本站规则且自行承担风险,本站不退款、不进行额外附加服务;查看《如何避免下载的几个坑》。如果您已付费下载过本站文档,您可以点击 这里二次下载。
- 4、如文档侵犯商业秘密、侵犯著作权、侵犯人身权等,请点击“版权申诉”(推荐),也可以打举报电话:400-050-0827(电话支持时间:9:00-18:30)。
- 5、该文档为VIP文档,如果想要下载,成为VIP会员后,下载免费。
- 6、成为VIP后,下载本文档将扣除1次下载权益。下载后,不支持退款、换文档。如有疑问请联系我们。
- 7、成为VIP后,您将拥有八大权益,权益包括:VIP文档下载权益、阅读免打扰、文档格式转换、高级专利检索、专属身份标志、高级客服、多端互通、版权登记。
- 8、VIP文档为合作方或网友上传,每下载1次, 网站将根据用户上传文档的质量评分、类型等,对文档贡献者给予高额补贴、流量扶持。如果你也想贡献VIP文档。上传文档
查看更多
GaugePlateDataSheet-CoventryGrinders.doc
UNIT 17-18 LIFFORD WAY
BINLEY INDUSTRIAL ESTATE
COVENTRY CV3 2RN
TEL: 024 7623 3933 FAX: 024 7623 3928
E-mail: info@coventry-grinders.co.uk
Visit our site, www.coventry-grinders.co.uk
Company Reg no. 3129960 VAT Reg no. 487 623 115
GAUGE PLATE 01 (Ground Flat Stock)
A.I.S.I Type 01 Ground Flat Stock has a maximum Brinell hardness of 229 HB and it could go to as low as about 190 Brinell H.B. The hardness range on the Rockwell C scale ranges from 14-20
Gauge Plate is an oil hardening, low distortion, precision ground high integrity cold work tool steel widely used for the manufacture of numerous types of industrial tooling.
Main characteristics and properties of the material are;
High quenched hardness.
Low dimensional movement or distortion after hardening.
Hardens from a relatively low hardening temperature.
Good machinability in the as supplied condition.
These properties are due to the steels balanced composition which is basically a high carbon steel with the addition of manganese giving some of the properties mentioned above. The additions of Tungsten, Chromium and Vanadium give the steel increased wear resistance, hardenability and the ability to resist growth. The steel is supplied in the fully annealed condition with a maximum Brinell hardness of 229HB (50 tons per sq. inch tensile strength)
TYPICAL ANALYSIS AISI TYPE 01
Carbon .85% / 1.05%
Manganese 1.00% / 1.40%
Tungsten .40% / .60%
Chromium .40% / .60%
Vanadium .15% / .30%
The material conforms to AISI 01, BS4659 B01, Din Werkstoff no. 1.2510
HEAT TREATMENT
Annealing
The steel is supplied in the annealed condition but if it is necessary to re-anneal, the parts should be given some protection such as packing in cast iron turnings. The parts should then be heated to 780° - 800° C, equalized to ensure through heating and held at the this temperature for a further 1 hour. Following this the work is cooled slowly in the furnace at a rate not exceeding 25° per hour for th
您可能关注的文档
- FlowFields-TheColorfulFluidMixingGallery.ppt
- FluorescentGenotyping(SimplexPCR,MultiplexGel).doc
- FM200FireExtinguishingSystem-Chrysler.doc
- FoldedMountains.doc
- Folding,Faulting,andMountains-FAU-Departmentof.ppt
- Folds,Faults,andGeologicMaps-BakersfieldCollege.doc
- FoldsandFaults.ppt
- Foldsandfaultsarebothstructuresproducedbythe.doc
- Folie1-polandplus.kic-innoenergy.agh.edu.pl.ppt
- FoodAllergyFactsandStatisticsfortheU.S.PDF
- 外研社版高一必修1-Module-4-A-Social-Survey-My-Neighborhood.pptx
- 医务人员应知应会访谈培训教材.ppt
- 中医内科学心悸胸痹不寐.ppt
- 九年级英语全册-Unit-6-When-was-it-invented第一课时PPT人教新目标版.pptx
- 乡村振兴战略下农村特色产业发展中的政府职能研究——以平度市大泽山镇为例.pdf
- 信迪利单抗联合化疗对比DOS方案在局部晚期胃癌或胃食管结合部癌新辅助治疗中的疗效和安全性.pdf
- 嗜热毁丝霉6-磷酸果糖激酶-2基因功能研究.pdf
- 双平台竞争下供应商的广告合作策略研究.pdf
- 乡村幼儿家庭劳动教育现状、问题及对策研究——以青西新区Z镇幼儿园家庭为例.pdf
- 产权连锁酒店营销专题方案.docx
文档评论(0)