温拌沥青混合料研究.docVIP

温拌沥青混合料研究 　　摘要：温拌沥青混合料是一种节能环保的新型沥青材料，与传统的热拌沥青混合料和冷拌沥青混合料相比，具有十分显著的生态优势和更广阔的应用前景，弥补了传统材料的不足，其研发与应用对于集约型社会建设具有重大意义，本文将从技术原理、生产材料、应用领域以及优势和不足等方面对温拌沥青混合料进行全面研究。 　　 　　关键词： 沥青混合料，温拌，应用，节能环保 　　Abstract: Warm mix asphalt mixture is a new type energy-saving asphalt material, and compare with traditional hot mix asphalt mixture and cold asphalt mixtures, it has obvious ecological advantages and broad prospects, make up for the traditional material deficiencies, its development and application has great significance for the intensive social construction, this article from the technical principle, production materials, application and the advantages and disadvantages of warm mix asphalt mixture to undertake a comprehensive study. 　　Key words: asphalt mixture; mixing temperature; application; energy saving and environmental protection 　　 　　中图分类号 : P632+.6文献标识码： A 文章编号： 　　 　　 　　一直以来，热拌沥青混合料在道路施工中有着十分广泛的应用，然而，随着生态环保理念的深入人心，热拌沥青混合料高污染、高能耗的缺陷使得它已不能再满足社会生产的要求，而与之相反的冷拌沥青混合料虽然低污染、低能耗，但其综合性能较低，无法保证施工质量，因此，人们开始研发一种新的沥青材料来弥补传统材料的缺陷，于是，温拌沥青混合料应运而生。温拌沥青混合料通过一定的技术手段，降低了沥青的粘度，使其可以在相对较低的温度下进行搅拌和施工，在目前的实践中，温拌沥青混合料的拌和温度为110℃―130℃，施工温度为90℃ ―100℃，处于热拌沥青混合料与冷拌沥青混合料之间，但其性能却可以达到甚至超过热拌沥青混合料。与传统沥青材料相比，温拌沥青混合料具有更高的环保效益和更广泛的应用前景。 　　一、温拌沥青混合料的技术原理及技术类型 　　温拌沥青混合料是运用一定的方法，在将对较低的温度环境中降低沥青的粘度，来实现沥青与混合料的拌和的，其原理主要有两种：其一，是通过熔点较低的添加剂的作用改变沥青的粘度曲线，从而实现在较低温度下的拌和；其二，是在拌和过程中，通过载体或引入水分与沥青接触产生蒸汽的方式，使沥青膨胀形成泡沫，从而更容易在低温下充分包裹集料。 　　就目前国内外的研发技术水平来讲，温拌沥青混合料的技术方法主要有泡沫沥青温拌技术、有机添加剂法、沥青―矿物法、乳化沥青拌和法以及低能量沥青技术等几种，其中，乳化沥青温拌技术已经获得了较为广泛的研究与应用。 　　二、温拌沥青混合料的优势 　　2.1环保优势 　　温拌沥青混合料可以减少有害物排放。沥青当中含有大量的碳、硫、氮等元素，在高温生产和施工过程中，会释放出大量的有害气体，造成环境污染，并且，有关测试表明，在沥青混合料的生产过程中，温度每提高10摄氏度，每吨材料的二氧化碳的排放量将增加0.9千克，温拌沥青混合料的低温拌和及施工显著降低了有害气体的排放量。温拌沥青混合料的生产可以降低能耗。传统的热拌沥青混合料是一种热拌热铺的材料，在生产和施工过程中要求保持很高的温度，对能源的消耗很大，研究显示，每吨沥青混凝土的产生就要有近8升的燃油被消耗掉，而温拌沥青混合料的拌和温度被降低了30℃ ―50℃，对能源的消耗可降低30％，对于可持续发展具有十分重大的作用。 　　2.2应用优势 　　改善施工环境。温拌沥青混合料的摊铺、压实过程对温度的要求降低，同时有害气体和粉尘的排放量也减少，这就大大改善了施工作业的环境，不仅有利于提高工作效率，方便组织施工，也有利于保障施工人员的健康。降低施工的季节局限性。温拌技术缩小了沥青温度与外界环境温度之间的差距，温拌沥青混合料在运输中