含稀土配合物聚合物透明材料的设计合成及发光性能的研究资料.pptVIP

* * 与直接掺杂法荧光强度的比较 Table 3-1 The comparison of the luminescence properties of the composite resin by doping and by in situ composite method *The content of lanthanide complex is 0.31 wt% 第二部分 * * Table 3-2 The luminescence properties of optical resin containing rare earth complex Eu3+ by in situ composite method * The concentration of the lanthanide complexes is 2.5×10-5 mol/L 不同的有机配体对含铕配合物复合树脂的荧光性质的影响 第二部分 * * Table 3-3 The luminescence properties of optical resin containing rare earth complex Tb3+ by in situ composite method * The concentration of the lanthanide complexes is 2.5×10-5 mol/L 第二部分 不同的有机配体对含铽配合物复合树脂的荧光性质的影响 * * Fig 3-6 The decay curves of the composite resin containing (a) Tb3+-2(phen)-MA/ St and (b) the composite resin containing Tb(phen)2 第二部分 复合树脂的荧光寿命 * * 复合树脂的微观形态 Fig3-7 TEM photo of the polymer liquid containing Tb3+-2.0(phen)-MA/St (after copolymerization reaction were taken place 2.5 h) (a), and the composite resin containing Tb3+-2.0(phen)-MA/St (b) 第二部分 * * 在MA/St共聚体系中建立了原位复合法制备含稀土配合物的光学树脂的新方法。 在相同配合物含量情况下，其荧光强度明显高于直接掺杂法的光学树脂，且荧光寿命明显延长。 Tb3+ 配合物的复合树脂的荧光发射强度明显高于相应的Eu3+ 配合物的复合树脂。 MA 只有通过与phen 等形成协同配体时，才能达到敏化稀土发光的效果。 通过对原位复合法制备的光学树脂中配合物的微观形态研究，发现稀土配合物以小于20 nm的尺寸均匀地分散在聚合物体系中。 本章小结 第二部分 * * 第三部分 稀土配合物纳米微晶的合成及其在光学树脂中的复合 * * 3 纳米微晶在光学树脂中的复合设 计 思 想 合成稀土配合物纳米微晶 又用两亲性分子对纳米微晶进行修饰 将纳米微晶和配合物与光学树脂复合 对材料的光学、磁学和微观形态等进行研究 -文献综述- 本工作的方法 纳米微晶 修饰后 配合物 光学树脂 高稀土配合物含量的光学树脂 有利于稀土配合物光、电、磁以及激光性质的展现 * * 纳米微晶及配合物的结构表征 Fig 4-1 The infrared spectra of organic ligand DBM (A)，surfactant CPC (B), Eu(DBM)3.H2O (30nm) (C) and Eu(DBM)4.CPC (D) -第三部分- Table 4-1 Elementary analysis data of nanocrystal and complex 元 素 配合物 C H N RE Eu(DBM)3.H2O 64.63 4.56 0 17.98 64.13 4.52 0 18.05 Eu(DBM)4.CPC 70.03 6.20 1.008 22.76 69.67 6.64 1.113 22.58 Eu(DBM)3·2H2O 62.99 4.76 0 17.55 62.79 4.65 0 17.67 * * Fig 4-2 TGA of 100nm Eu(DBM)3.H2O , Eu(DBM)3.2H2O complex and Eu(DBM)4.CPC A. 30 nm Eu(DBM)3.H2O B. Eu(DBM)3.2H2O complex. C Eu(DBM)4.CPC 纳米微晶和配合