建筑用树脂基复合材料损伤性能与研究-园.docVIP

摘 要 建筑产业在国民经济的占很大比重。然而传统建筑材料由于其高能耗、高污染及生产效率低等缺点，从而使新型绿色高产的建筑材料具有广阔的发展空间。玻璃纤维增强复合材料比强度、比模量抗疲劳性能等，建筑。然而复合材料在制造工艺及各向载荷的影响下，在运转过程中难免出现纤维断裂、分层等结构损伤，进而导致断裂或失稳破坏。针对这一问题，本文采用声发射技术对加载破坏条件下的含分层复合材料进行健康检测。 本文利用声发射技术对含单个分层复合材料试件进行全程监测，研究复合材料弯曲加载下的力学响应行为、损伤破坏特征和对应的声发射特性。结果表明，力学性能的影响不大，但其损伤破坏形式明显不同。埋藏较浅的分层缺陷会导致高应力纤维的过早断裂和分层的大面积扩展；随分层深度的增加，声发射事件明显减少，声发射源主要分布在断裂部位及其相邻区域。声发射计数率、幅度分布、相对能量和撞击源定位信号等特征与复合材料试件的弯曲损伤破坏相对应。本文还对纤维铺向不同的试样三点弯曲破坏声发射，分析的方法。结果表明，不同试样应力应变关系表现出明显不同，声发射中的信号以及信号特（包括幅度、能量、持续时间）也有着明显的不同，而且从声发射信号的参数特征来看的损伤破坏阶段性，信号的特。 Damage Research of Resin Matrix Composite Material in Architecture Abstract The construction industry accounts for a large proportion of the national economy. traditional Building materials have many disadvantages like high energy consumption, high pollution and low efficiency of production, so the New type of building materials which are green and high-producing have a broad space for development. Glass fiber reinforced composite material becomes the most commonly used material of architectural construction because of its advantages like high specific strength, high specific modulus and good fatigue resistance performance. But the composite under the influence of manufacturing process and wind load, it would appear structural damage such as fiber fracture and delamination, and then caused fracture or buckling failure. In order to solve this problem, this paper monitored the composite with delamination by the Acoustic emission (AE) technology. In this study, AE was used to monitor the three point bending test of delaminated composite material with a single delamination defect. The mechanical response behavior, damage and failure characteristics, and the corresponding AE characteristics of the composite materials have been investigated. The results show that the location of the delamination defect has little effect on the mechanical properties of the composite materials, whereas the damage failure mode is significantly different. The shallow delaminatio