低品位金矿柱浸试验.docVIP

doi：10.3969/j.issn.1007-7545.2016.07.011 低品位金矿柱浸试验 林泓富1,2 （1.紫金矿业集团股份有限公司，福建上杭 364200；2.福州大学 紫金矿业学院，福州 350108） 摘要：对某低品位金矿进行柱浸试验研究，考察喷淋制度对金、铜浸出率的影响，探索了在现行堆浸条件下矿石浸出的可行性。结果表明，采用现行堆浸技术处理低品位金矿石是可行的，在合适的喷淋制度下，20天内金的浸出率可达84%以上。 关键词：低品位金矿；柱浸；浸出率 中图分类号：TF831 文献标志码：A 文章编号：1007-7545（2016）07-0000-00 Column Leaching Experiment for Low-Grade Gold Ore LIN Hong-fu1,2 （1. Zijin Mining Group Co. Ltd., Shanghang 364200, Fujian, China; 2. College of Zijin Mining, Fuzhou University, Fuzhou 350108, China） Abstract：Column leaching experiment for low-grade gold ore was carried out. The effects of spray methods on gold and copper leaching rates were investigated. Leaching feasibility under current heap leaching conditions was explored. The results show that it is feasible to recover gold from this gold ore by heap leaching. Gold leaching rate within 20 days is 84% above with suitable spray methods. Key words：low-grade gold ore; column leaching; leaching rate 随着金矿资源被大量地开发和利用，高品位易处理金矿越来越少，低品位难处理金矿石[1]的开发已成为黄金矿产资源开发的热点。紫金山金矿金储量大，目前，金矿选厂采用堆浸工艺[2-6]处理粗粒矿石，矿石金平均品位约为0.35 g/t，但是随着金矿的大规模开发，金的保有储量越来越少，矿石金含量不断下降。因此，低品位金矿石（Au≤0.15 g/t）的利用被提上日程[7-8]。本文开展低品位金矿石可浸性研究，进一步明晰现行堆浸工艺条件下，金、铜的浸出行为[9-10]，验证现行工艺可行性，并为紫金山金铜矿圈矿工作提供技术依据。 1 试验原料与方法 试验样品为紫金山低品位金矿，金品位为0.12 g/t，铜品位为0.008%，属低金低铜矿石。破碎后的原矿（-50 mm）样的粒度筛析试验结果如表1所示。 表1 粒度筛析结果 Table 1 Results of sieve analysis 粒级/mm产率/%AuCu品位/(g·t-1)分配率/%品位/%分配率/%+25~-5032.810.0512.530.00936.31+10~-2520.990.1016.040.00820.65+2~-1015.170.1820.860.00814.93+0.074~-220.380.0914.010.00615.03-0.07410.640.4536.560.01013.08返算品位-0.13-0.008- 由表1可知，金和铜都会在小粒级矿中富集，说明矿物中的金和铜的粒度均较小，原矿中细泥（-0.074 mm）产量为10.64%。 物相分析结果表明，紫金山低品位金矿中主要矿物是石英（占比73.48%），还有少量地开石（占比11.62%）、绢云母（占比6.26%）、明矾石（占比4.44%）和赤铁矿（占比2.97%）等矿物。金的化学物相分析结果表明，82%的金以裸露金的形态存在，原则上这部分金都可以被浸出，硅酸盐及其它包裹金占比10.1%，硫化物和碳酸盐包裹金分别占5.5%和1.8%。 收稿日期：2016-02-04 基金项目：国家自然科学基金资助项目 作者简介：林泓富（1974-），男，福建永定人，硕士. 2 试验方法 柱浸试验在直径300 mm的柱子中进行，入柱粒度为-50 mm。模拟现场工艺参数，在特定喷淋制度下，每天测量浸出液体积，氰根浓度，并取50 mL左右样品