材料力学性能ppt.pptVIP

张成智 材料力学性能第二次小班课 遇到的专业词汇 1. lock dislocations 位错钉扎 2.impurities 杂质 3.diffused 扩散 4.positive-edge dislocation 刃型位错 5.lattice strain=the distortion in the matrix 晶格畸变 6.interstitial atom 间隙原子 7.crew dislocations 螺型位错 可垂耳理论的要素 How did Cottrell and Bilby derive their concept of yield-point phenomena that 1. lock dislocations by means of 2.impurities, such as C (or N) atoms? To better understand, consider Fig. 3.21a, where an interstitial impurity has 3.diffused into a dislocation and settled underneath. 如何用可垂耳理论得到屈服点现象的观念， 通过2.杂质原子在位错出聚集1.钉轧位错， 比如C或N原子。为了更好的解释，如图 3.21a，一个杂质原子3.扩散到位错那里， 并且固定在那里。 Elements of the Cottrell-Bilby Theory A positive-edge dislocation is 1.under tension just below it close to its core？ and under 2.compression above it. In Fig. 3.22, the stress just above an edge dislocation is under pressure and below it under tension is indicated. Read’s book provides a complete distribution of the 3.stress field and the 4.lattice strain. 一个刃型位错在靠近杂质原子？的 下面是在1.张力的作用下，并且在 它上面2.压缩。在图3.22中，可以 指出刃型位错上面受压下面受拉。 本书中提供了完整的3.应力场分布 和4.晶格畸变。 When randomly distributed, N or C also has a stress field, which can be reduced (relieved) when it settles in the immediate vicinity and below the dislocation core. This location of the1. interstitial atom under the dislocation which is under2.. dilation provides the lowest energy of the system. 当杂质原子均匀分布时，N或C也有一个应力场，它存在于位错附近和下面时可以降低自由能。1.间隙原子在这个位置引起的2.膨胀是系统能量最低的时候。 The C or N atoms, besides inducing1. volumetric expansion, also cause 2.tetragonal distortion. This is a consequence of the fact that C atoms are located in interstitial sites at the center of the 001planes (faces) and the [001] directions (edges), thus 3.distorting the unit cell tetragonally in a [001] direction. This kind of distortion allows reactions with shear and hydrostatic stress fields to occur. Therefore, a C impurity will interact with both edge and 4.crew dislocations. 这个C或N